GR442QR7LB102KW01L Datasheet, PDF (173/237 Pages) Murata Manufacturing Co., Ltd. – chip monolithic ceramic capacitors

!Note • Please read rating and !CAUTION (for storage, operating, rating, soldering, mounting and handling) in this catalog to prevent smoking and/or burning, etc.
• This catalog has only typical specifications. Therefore, please approve our product specifications or transact the approval sheet for product specifications before ordering.
C02E.pdf
Oct.1,2012
GR3 Series Specifications and Test Methods
No.
Item
Specifications
1
Operating
Temperature Range
2 Appearance
3 Dimensions
–55 to +125°C
No defects or abnormalities
Within the specified dimensions
4 Dielectric Strength No defects or abnormalities
5
Insulation Resistance
(I.R.)
More than 10,000MΩ or 100MΩs—&7HICHEVERISSMALLER
6 Capacitance
7
Dissipation
Factor (D.F.)
Within the specified tolerance
0.01 max.
Capacitance
8 Temperature
Characteristics
Cap. Change
Within
% ⁺²²
–33
(Temp. Range: –55 to +125°C)
9
Adhesive Strength
of Termination
No removal of the terminations or other defect should occur.
Appearance No defects or abnormalities
Capacitance Within the specified tolerance
10
Vibration
Resistance
D.F.
0.01 max.
Test Method
–
Visual inspection
Using calipers and micrometers
No failure should be observed when voltage in Table is applied
between the terminations for 1 to 5 sec., provided the
charge/discharge current is less than 50mA.
Rated Voltage
DC250V
DC450V
DC630V
Test Voltage
200% of the rated voltage
150% of the rated voltage
120% of the rated voltage
The insulation resistance should be measured with DC500±50V
(DC250±25V in case of rated voltage: DC250V, DC450V) and
within 60±5 sec. of charging.
The capacitance/D.F. should be measured at a frequency of
1±0.2kHz and a voltage of AC1±0.2V(r.m.s.).
The capacitance measurement should be made at each step
specified in the Table.
Step
1
2
3
4
5
Temperature (°C)
25±2
Min. Operating Temp.±3
25±2
Max. Operating Temp.±2
25±2
U*ÀiÌÀi>̓i˜Ì
Perform a heat treatment at 150⁺ –0 10°C for 60±5 min. and then
let sit for 24±2 hrs. at room condition.*
Solder the capacitor to the testing jig (glass epoxy board) shown
in Fig. 1.
Then apply 10N force in the direction of the arrow.
The soldering should be done using the reflow method and
should be conducted with care so that the soldering is uniform
and free of defects such as heat shock.
10N, 10±1s
Glass Epoxy Board
Fig. 1
Solder the capacitor to the test jig (glass epoxy board).
The capacitor should be subjected to a simple harmonic motion
having a total amplitude of 1.5mm, the frequency being varied
uniformly between the approximate limits of 10 and 55Hz. The
frequency range, from 10 to 55Hz and return to 10Hz, should be
traversed in approximately 1 min. This motion should be applied
for a period of 2 hrs. in each of 3 mutually perpendicular
directions (total of 6 hrs.).
Glass Epoxy Board
Solder resist
Cu
* "Room condition" Temperature: 15 to 35°C, Relative humidity: 45 to 75%, Atmospheric pressure: 86 to 106kPa
Continued on the following page.
155