DE1E3KX332MN5AA01 Datasheet, PDF (47/84 Pages) Murata Manufacturing Co., Ltd. – Safety Standard Certified Ceramic Capacitors/ High Voltage Ceramic Capacitors | |||
|
◁ |
!Note ⢠Please read rating and !CAUTION (for storage, operating, rating, soldering, mounting and handling) in this catalog to prevent smoking and/or burning, etc.
⢠This catalog has only typical speciï¬cations. Therefore, please approve our product speciï¬cations or transact the approval sheet for product speciï¬cations before ordering.
C85E.pdf
Apr.7,2014
DEA Series Speciï¬cations and Test Methods
Continued from the preceding page.
No.
Item
Specifications
Test Method
13
Soldering Effect
(On-Preheat)
Appearance
Capacitance
Change
Dielectric Strength
(Between Lead
Wires)
No marked defect
Within ±2.5%
Per item 4.
First the capacitor should be
stored at 120+0/-5°C for
60+0/-5 sec.
Then, as in the figure, the lead
wires should be immersed in
solder of 260+0/-5°C up to 1.5 to
2.0mm from the root of terminal
Thermal
Screen
Capacitor
1.5
to 2.0mm
Molten
Solder
for 7.5+0/-1 sec.
Post-treatment:
Capacitor should be stored for 1 to 2 hrs. at room condition.*1
14
Temperature
Cycle
Appearance
Capacitance
Change
Q
I.R.
Dielectric Strength
(Between Lead
Wires)
No marked defect
Within ±5%
275+5/2C*2min. (30pF under)
350 min. (30pF min.)
1000MΩ min.
Per item 4.
The capacitor should be subjected to 5 temperature cycles.
<Temperature Cycle>
Step Temperature (°C) Time (min)
1
-25±3
30
2
Room Temp.
3
3
125±3
30
4
Room Temp.
3
Post-treatment:
Cycle time: 5 cycles
Capacitor should be stored for 1 to 2 hrs. at room condition.*1
15
Humidity (Under
Steady State)
Appearance
Capacitance
Change
Q
I.R.
No marked defect
Within ±5%
275+5/2C*2min. (30pF under)
350 min. (30pF min.)
1000MΩ min.
Set the capacitor for 500+24/-0 hrs. at 40±2°C in 90 to 95%
relative humidity.
Post-treatment:
Capacitor should be stored for 1 to 2 hrs. at room condition.*1
16
Humidity
Loading
Appearance
Capacitance
Change
Q
I.R.
No marked defect
Within ±5%
275+5/2C*2min. (30pF under)
350 min. (30pF min.)
1000MΩ min.
Apply the rated voltage for 500+24/-0 hrs. at 40±2°C in 90 to
8
95% relative humidity.
(Charge/Discharge currentV50mA)
Post-treatment:
Capacitor should be stored for 1 to 2 hrs. at room condition.*1
17 Life
Appearance
Capacitance
Change
Q
I.R.
No marked defect
Within ±3%
275+5/2C*2min. (30pF under)
350 min. (30pF min.)
2000MΩ min.
Apply a DC voltage of 150% of the rated voltage for
1000+48/-0 hrs. at 125±2°C with a relative humidity of 50%
max. (Charge/Discharge currentV50mA)
Post-treatment:
Capacitor should be stored for 1 to 2 hrs. at room condition.*1
*1 "Room condition" Temperature: 15 to 35°C, Relative humidity: 45 to 75%, Atmospheric pressure: 86 to 106kPa
*2 "C" expresses nominal capacitance value (pF).
45
|
▷ |