DE1E3KX332MN5AA01 Datasheet, PDF (18/84 Pages) Murata Manufacturing Co., Ltd. – Safety Standard Certified Ceramic Capacitors/ High Voltage Ceramic Capacitors

!Note • Please read rating and !CAUTION (for storage, operating, rating, soldering, mounting and handling) in this catalog to prevent smoking and/or burning, etc.
• This catalog has only typical specifications. Therefore, please approve our product specifications or transact the approval sheet for product specifications before ordering.
C85E.pdf
Apr.7,2014
Type KY/KH/KX Specifications and Test Methods
Continued from the preceding page.
No.
Item
Specifications
Appearance No marked defect
Capacitance
Change
Within ±10%
Soldering
I.R.
9 Effect
(Non-Preheat)
Dielectric
Strength
1000MΩ min.
Per Item 6
Soldering
10 Effect
(On-Preheat)
Appearance
Capacitance
Change
I.R.
Dielectric
Strength
No marked defect
Within ±10%
1000MΩ min.
Per Item 6
Appearance No marked defect
Test Method
As shown in the figure, the lead
wires should be immersed in
Thermal
solder of 350±10°C or 260±5°C up ^Screen
to 1.5 to 2.0mm from the root of
terminal for 3.5±0.5 sec. (10±1
sec. for 260±5°C).
Capacitor
1.5
to 2.0mm
Molten
Solder
Pre-treatment:
Capacitor should be stored at 85±2°C for 1 hr., then placed at
room condition*² for 24±2 hrs. before initial measurements.
Post-treatment:
Capacitor should be stored for 1 to 2 hrs. at room condition.*²
First the capacitor should be
stored at 120+0/-5°C for
60+0/-5 sec.
Then, as in the figure, the lead
wires should be immersed in
solder of 260+0/-5°C up to 1.5 to
Thermal
Screen
Capacitor
1.5
to 2.0mm
Molten
Solder
2.0mm from the root of terminal
for 7.5+0/-1 sec.
Pre-treatment:
Capacitor should be stored at 85±2°C for 1 hr., then placed at
room condition*² for 24±2 hrs. before initial measurements.
Post-treatment:
Capacitor should be stored for 1 to 2 hrs. at room condition.*²
11
Vibration
Resistance
Capacitance Within the specified tolerance
Char.
Specifications
D.F.
Q
B, E
D.F.V2.5%
F
D.F.V5.0%
SL
QU400+20C*¹(CF30pF)
QU1000 (CU30pF)
The capacitor should be firmly soldered to the supporting lead
wire and vibrated at a frequency range of 10 to 55Hz, 1.5mm in
total amplitude, with about a 1-minute rate of vibration change
from 10Hz to 55Hz and back to 10Hz.
Apply for a total of 6 hrs., 2 hrs. each in 3 mutually
perpendicular directions.
Appearance No marked defect
Humidity
12
(Under
Steady
State)
Capacitance
Change
D.F.
Q
Char.
B
E, F
SL
Capacitance Change
Within ±10%
Within ±15%
Within ± 5%
Char.
B, E
F
SL
Specifications
D.F.V5.0%
D.F.V7.5%
QU275+5/2C*¹(CF30pF)
QU350
(CU30pF)
Set the capacitor for 500±12 hrs. at 40±2°C in 90 to 95%
relative humidity.
Post-treatment:
Capacitor should be stored for 1 to 2 hrs. at room condition.*²
I.R.
Dielectric
Strength
Appearance
3000MΩ min.
Per Item 6
No marked defect
Capacitance
Change
13
Humidity
Loading
D.F.
Q
Char.
B
E, F
SL
Capacitance Change
Within ±10%
Within ±15%
Within ± 5%
Char.
B, E
F
SL
Specifications
D.F.V5.0%
D.F.V7.5%
QU275+5/2C*¹(CF30pF)
QU350
(CU30pF)
Apply the rated voltage for 500±12 hrs. at 40±2°C in 90 to 95%
relative humidity.
Post-treatment:
Capacitor should be stored for 1 to 2 hrs. at room condition.*²
I.R.
3000MΩ min.
Dielectric
Strength
Per Item 6
*¹ "C" expresses nominal capacitance value (pF).
*² "Room condition" Temperature: 15 to 35°C, Relative humidity: 45 to 75%, Atmospheric pressure: 86 to 106kPa
Continued on the following page.
16