GQM1885C2A6R2DB01D Datasheet, PDF (20/29 Pages) Murata Manufacturing Co., Ltd. – CHIP MONOLITHIC CERAMIC CAPACITOR FOR GENERAL | |||
|
◁ |
! Caution
4-3.Correction with a Soldering Iron
1. When sudden heat is applied to the components when using a soldering iron, the mechanical strength of
the components will decrease because the extreme temperature change can cause deformations inside the
components. In order to prevent mechanical damage to the components, preheating is required for both
the components and the PCB board. Preheating conditions, (The "Temperature of the Soldering Iron tip",
"Preheating Temperature", "Temperature Differential" between the iron tip and the components and the
PCB), should be within the conditions of table 3. It is required to keep the temperature differential
between the soldering Iron and the component surfaces (ÎT) as small as possible.
2. After soldering, do not allow the component/PCB to rapidly cool down.
3. The operating time for the re-working should be as short as possible. When re-working time is
too long, it may cause solder leaching, and that will cause a reduction in the adhesive
strength of the terminations.
Table 3
Part Number
GRâ¡03/15/18/21/31
Temperature
of Soldering
Iron tip
350â max.
Preheating
Temperature
150â min.
Temperature
Differential
(ÎT)
ÎTâ¦190â
Atmosphere
Air
GRâ¡32/43/55
280â max. 150â min. ÎTâ¦130â
Air
*Applicable for both Pb-Sn and Lead Free Solder.Pb-Sn Solder: Sn-37Pb
Lead Free Solder: Sn-3.0Ag-0.5Cu
4. Optimum Solder amount when re-working with a Soldering lron
4-1. In case of sizes smaller than 0603, (GRâ¡03/15/18),
the top of the solder fillet should be lower than 2/3's
of the thickness of the component or 0.5mm whichever
is smaller. In case of 0805 and larger sizes, (GRâ¡21/
31/32/43/55), the top of the solder fillet should be lower
than 2/3's of the thickness of the component. If the
solder amount is excessive, the risk of cracking is higher
during board bending or under any other stressful condition.
Solder Amount
in section
4-2. A Soldering iron with a tip of ø3mm or smaller should be used. It is also necessary to keep
the soldering iron from touching the components during the re-work.
4-3. Solder wire with ø0.5mm or smaller is required for soldering.
4-4.Leaded Component Insertion
1. If the PCB is flexed when leaded components (such as transformers and ICs) are being mounted,
chips may crack and solder joints may break.
Before mounting leaded components, support the PCB using backup pins or special jigs to prevent warping.