C5750X7R1H106M Datasheet, PDF (64/72 Pages) TDK Electronics – C Series General Application

General
Specifications
C Series – General Application
No. Item
11
Solderability
Performance
New solder to cover over 75% of
termination.
25% may have pinholes or rough spots
but not concentrated in one spot.
Ceramic surface of A sections shall not
be exposed due to melting or shifting of
termination material.
Test or Inspection Method
Completely soak both terminations in
solder at 235±5ºC for 2±0.5s.
Solder: H63A (JIS Z 3282)
Flux: Isopropyl alcohol (JIS K 8839)
Rosin (JIS K 5902) 25% solid solution.
A section
12
Resistance to solder heat
Completely soak both terminations in solder at
External
260±5ºC for 5±1s.
No cracks are allowed and terminations
appearance
shall be covered at least 60% with new Preheating condition
solder.
Temp.: 150±10ºC
Capacitance
Characteristics
Class 1 C0G
Class 2 X5R
X7R
Y5V
Change from the
value before test
Capacitance drift within
±2.5% or ±0.25pF,
whichever larger.
± 7.5 %
± 7.5 %
± 20 %
Time: 1 to 2min.
Flux: Isopropyl alcohol (JIS K 8839)
Rosin (JIS K 5902) 25% solid solution.
Solder: H63A (JIS Z 3282)
Leave the capacitor in ambient conditions for 6 to 24h
(Class 1) or 24±2h (Class 2) before measurement.
Q (Class 1)
D.F. (Class 2)
Insulation
Resistance
Voltage
Proof
Rated Capacitance
C ≥ 30pF
C < 30pF
Q
1,000 min.
400+20×C min.
C : Rated capacitance (pF)
Meet the initial spec.
Meet the initial spec.
No insulation breakdown or other
damage.
TDK MLCC US Catalog
Page 66
Version B11