AC0402BRNPO5BN Datasheet, PDF (19/24 Pages) YAGEO Corporation – SURFACE MOUNT MULTILAYER CERAMIC CAPACITORS

Product specification 19
Surface-Mount Ceramic Multilayer Capacitors ^{Automotive grade NP0/X7R 6.3 V to 630 V}
24
TEST
TEST METHOD
Operational Life _{AEC-Q200 8}
PROCEDURE
1. Preconditioning, class 2 only:
150 +0/-10 °C /1 hour, then keep for
24 ± 1 hour at room temp
2. Initial measure:
Spec: refer to initial spec C, D, IR
3. Endurance test:
Temperature: X7R: 125 °C
Specified stress voltage applied for 1,000 hours:
Applied 2.0 x U_r for general products
Applied 1.5 x U_r for high cap. Products
High voltage series follows with below
stress condition:
Applied 1.5 x Ur for 200V, 250V series
Applied 1.3 x Ur for 500V, 630V series
Applied 1.2 x Ur for 1KV, 2KV, 3KV series
4. Recovery time: 24 ± 2 hours
5. Final measure: C, D, IR
REQUIREMENTS
No visual damage
∆C/C
NP0: Within ± 2% or 1 pF,
whichever is greater
X7R: ± 15%
D.F.
NP0: ≤ 2 x specified value.
X7R: ≤ 16V: ≤ 7%
≥ 25V: ≤ 5%
IR
NP0: ≥ 4,000 MΩ or IR x C_r ≥
40s whichever is less
X7R: ≥ 1,000 MΩ or IRx C_r ≥
50s whichever is less
External Visual
Physical
Dimension
AEC-Q200 9
AEC-Q200 10
Note: If the capacitance value is less than the minimum value
permitted, then after the other measurements have been
made the capacitor shall be preconditioned according to “IEC
60384 4.1” and then the requirement shall be met.
Any applicable method using × 10 magnification
In accordance with
specification
Verify physical dimensions to the applicable device
specification.
In accordance with
specification
Mechanical
Shock
Vibration
AEC-Q200 13
AEC-Q200 14
Three shocks in each direction shall be applied along the three
mutually perpendicular axes of the test specimen (18 shocks)
Peak value: 1,500 g’s
Duration: 0.5 ms
Velocity change: 15.4 ft/s
Waveform: Half-sin
∆C/C
NP0: Within ± 0.5% or 0.5 pF,
whichever is greater
X7R: ± 10%
D.F.
Within initial specified value
IR
Within initial specified value
5 g’s for 20 minutes, 12 cycles each of 3 orientations.
Note:
Use 8” x 5” PCB. 0.31” thick 7 secure points on one long side
and 2 secure points at corners of opposite sides. Parts
mounted within 2” from any secure point. Test from
10-2000 Hz.
∆C/C
NP0: Within ± 0.5% or 0.5 pF,
whichever is greater
X7R: ± 10%
D.F: meet initial specified value
IR meet initial specified value
Mar. 31, 2017 V.6