CC1210KKX5R7BB226 Datasheet, PDF (15/17 Pages) YAGEO Corporation – SURFACE-MOUNT CERAMIC MULTILAYER CAPACITORS

Product specification 15
Surface-Mount Ceramic Multilayer Capacitors ^{High-Capacitance X5R/X7R 6.3 V to 25 V}
17
Table 14 Test condition, procedure and requirements (continued)
TEST
TEST METHOD
PROCEDURE
Resistance to
soldering heat
4.9
Precondition: 150 +0/–10 °C for 1 hour, then keep for 24
±1 hours at room temperature
Preheating: for size ≤ 1206: 120 to 150 °C for 1 minute
Preheating: for size >1206: 100 to 120 °C for 1 minute
and 170 to 200 °C for 1 minute
Solder bath temperature: 260 ±5 °C
Dipping time: 10 ±0.5 seconds
Recovery time: 24 ±2 hours.
REQUIREMENTS
The termination shall be well
tinned
X5R/X7R: lΔC/Cl: ≤ 10%
Y5V: lΔC/Cl: ≤ 20%
D.F.: within initial specified value
R_ins: within initial specified value
Solderability
4.10 Unmounted chips completely immersed in a solder bath at The termination shall be well
235 ±5 °C
tinned.
Dipping time: size ≤ 1206 for 2 ±0.5 seconds; size > 1206
for 4 ±0.5 seconds
Rapid change IEC 60384-22 4.11
of
temperature
Preconditioning;
150 +0/–10 °C for 1 hour, then keep for 24 ±1 hours at
room temperature
5 cycles with following detail:
30 minutes at lower category temperature;
30 minutes at upper category temperature
Recovery time 24 ±2 hours.
No visual damage
X5R/X7R: ≤ 15%
Y5V: ≤ 20%
D.F.: within initial specified value
R_ins: within initial specified value
Damp heat
steady state
4.13 Initial measurements; after 150 +0/-10 °C for 1 hour, then X5R/X7R: lΔC/Cl: ±20%
keep for 24 ±1 hours at room temperature
Y5V: lΔC/Cl: ±30%
Duration and conditions: 500 ±12 hours at 40 ±2 °C;
90 to 95% RH
Final measurement: perform a heat treatment at 150 +0/–
10 °C for 1 hour, final measurements shall be carried out
D.F.: 2 × initial value max.
R_ins: 1,000 MΩ or R_ins × C_r ≥ 50
seconds, whichever is less
24 ±1 hours after recovery at room temperature without
load.
Endurance
4.14 Preconditioning;
X5R/X7R: lΔC/Cl: ±20%
Initial measurements; after 150 +0/-10 °C for 1 hour, then
keep for 24 ±1 hours at room temperature
Duration and conditions: 1,000 ±12 hours at upper
category temperature with 1.5 × U_r voltage applied
Final measurement: perform a heat treatment at 150 +0/–
Y5V: lΔC/Cl: ±30%
D.F.: 2 × initial value max.
R_ins: 1,000 MΩ or R_ins × C_r ≥ 50
seconds, whichever is less
10 °C for 1 hour, final measurements shall be carried out
24 ±1 hours after recovery at room temperature without
load.
June 1, 2006 V.11
www.yageo.com