CC1210KKX5R7BB226 Datasheet, PDF (14/17 Pages) YAGEO Corporation – SURFACE-MOUNT CERAMIC MULTILAYER CAPACITORS

Product specification 14
Surface-Mount Ceramic Multilayer Capacitors ^{High-Capacitance X5R/X7R 6.3 V to 25 V}
17
SOLDERING RECOMMENDATION
Table 13
SOLDERING
METHOD
SIZE
0402
Reflow
≥ 0.1 µF
Reflow/Wave
< 0.1 µF
0603
≥ 1.0 µF
< 1.0 µF
0805
≥ 2.2 µF
< 2.2 µF
1206
≥ 4.7 µF
< 4.7 µF
≥ 1210
Reflow only
---
TESTS AND REQUIREMENTS
Table 14 Test condition, procedure and requirements
TEST
TEST METHOD
PROCEDURE
Mounting IEC 60384-22 4.3
The capacitors may be mounted on printed-circuit boards or
ceramic substrates
REQUIREMENTS
No visible damage
Visual
inspection and
dimension
check
4.4
Any applicable method using × 10 magnification
In accordance with
specification
Capacitance
4.5.1 Precondition: 150 +0/–10 °C for 1 hour, then keep for 48 ±1 Within specified tolerance
hours at room temperature
f = 1 kHz for C ≤10 µF: measuring voltage 1 V_rms at 20 °C
f = 120 Hz for C >10 µF: measuring voltage 0.5 V_rms at 20 °C
Dissipation
factor (D.F.)
Insulation
resistance
4.5.2 f = 1 kHz for C ≤10 µF: measuring voltage 1 V_rms at 20 °C
In accordance with
f = 120 Hz for C >10 µF: measuring voltage 0.5 V_rms at 20 °C ^{specification}
4.5.3 At U_r (DC) for 1 minute
In accordance with
specification
Voltage proof
Temperature
characteristic
Adhesion
4.5.4.2 2.5 × U_r for 1 minute
4.6
Between minimum and maximum temperature
4.15 A force applied for 10 seconds to the line joining the
terminations and in a plane parallel to the substrate
for size ≥ 0603: a force of 5 N applied
for size 0402: a force of 2.5 N applied
No breakdown or flashover
In accordance with
specification
No visible damage
Bond strength
of plating on
end face
4.8
Mounting in accordance with IEC 60384-22 paragraph 4.3
No visible damage
Conditions: bending 1 mm at a rate of 1 mm/s, radius jig 340
mm
X5R/X7R: lΔC/Cl: ≤ 10%
Y5V: lΔC/Cl: ≤ 20%
June 1, 2006 V.11