CA0612KRX7R8BB473 Datasheet, PDF (15/17 Pages) YAGEO Corporation – SURFACE-MOUNT CERAMIC MULTILAYER CAPACITORS

Surface-Mount Ceramic Multilayer Capacitors ^4C-Array
NP0/X7R/Y5V
Product specification 15
16 V to 50 V
17
TEST
Rapid change
of
temperature
TEST METHOD
IEC 60384- 4.11
21/22
PROCEDURE
Preconditioning;
150 +0/–10 °C for 1 hour, then keep for
24 ±1 hours at room temperature
5 cycles with following detail:
30 minutes at lower category temperature
30 minutes at upper category temperature
Recovery time 24 ±2 hours
REQUIREMENTS
No visual damage
<General purpose series>
∆C/C
Class 1:
NP0: within ±1% or 1 pF, whichever is greater
Class2:
X5R/X7R: ±15%
Y5V: ±20%
<High Capacitance series>
∆C/C
Class2:
X5R/X7R: ±15%
Y5V: ±20%
Damp heat
with U_r load
D.F. meet initial specified value
R_ins meet initial specified value
4.13 _{1. Preconditioning, class 2 only:}
No visual damage after recovery
150 +0/-10 °C /1 hour, then keep for
24 ±1 hour at room temp
<General purpose series>
2. Initial measure:
∆C/C
Spec: refer initial spec C, D, IR
Class 1:
3. Damp heat test:
NP0: within ±2% or 1 pF, whichever is greater
500 ±12 hours at 40 ±2 °C;
Class2:
90 to 95% R.H. 1.0 U_r applied
X5R/X7R: ±15%; Y5V: ±30%
4. Recovery:
Class 1: 6 to 24 hours
Class 2: 24 ±2 hours
5. Final measure: C, D, IR
D.F.
Class 1: NP0: ≤ 2 x specified value
Class2:
X5R/X7R: ≤ 16V: ≤ 7%
P.S. If the capacitance value is less than the
minimum value permitted, then after the
other measurements have been made the
capacitor shall be precondition according to
“IEC 60384 4.1” and then the requirement
shall be met.
≥ 25V: ≤ 5%
Y5V: ≤ 15%
R_ins
Class 1:
NP0: ≥ 2,500 MΩ or R_ins x C_r ≥ 25s whichever is less
Class2:
X5R/X7R/Y5V: ≥ 500 MΩ or R_ins x C_r ≥ 25s
whichever is less
<High Capacitance series>
∆C/C
Class2: X5R/X7R: ±20%; Y5V: ±30%
D.F.
Class2: 2 x initial value max
R_ins
Class2: 500 MΩ or R_ins x C_r ≥ 25s, whichever is less
Feb 05, 2010 V.1
www.yageo.com