CA0612KRX7R8BB473 Datasheet, PDF (14/17 Pages) YAGEO Corporation – SURFACE-MOUNT CERAMIC MULTILAYER CAPACITORS

Surface-Mount Ceramic Multilayer Capacitors ^4C-Array
NP0/X7R/Y5V
Product specification 14
16 V to 50 V
17
TEST
Bond
strength of
plating on
end face
TEST METHOD PROCEDURE
IEC 60384- 4.8 Mounting in accordance with IEC 60384-22
21/22
paragraph 4.3
Conditions: bending 1 mm at a rate of 1 mm/s,
radius jig 340 mm
REQUIREMENTS
No visible damage
<General purpose series>
∆C/C
Class 1:
NP0: within ±1% or 0.5 pF, whichever is greater
Class2:
X5R/X7R/Y5V: ±10%
<High Capacitance series>
∆C/C
Class2:
X5R/X7R/Y5V: ±10%
Resistance to
soldering
heat
Solderability
4.9 Precondition: 150 +0/–10 °C for 1 hour, then
Dissolution of the end face plating shall not
keep for 24 ±1 hours at room temperature
exceed 25% of the length of the edge
Preheating: for size ≤ 1206: 120 °C to 150 °C for ^concerned
1 minute
Preheating: for size >1206: 100 °C to 120 °C for
1 minute and 170 °C to 200 °C for 1 minute
Solder bath temperature: 260 ±5 °C
Dipping time: 10 ±0.5 seconds
Recovery time: 24 ±2 hours
<General purpose series>
∆C/C
Class 1:
NP0: within ±0.5% or 0.5 pF, whichever is greater
Class2:
X5R/X7R: ±10%
Y5V: ±20%
<High Capacitance series>
∆C/C
Class2:
X5R/X7R: ±10%
Y5V: ±20%
4.10 Preheated the temperature of 80 °C to 140 °C
and maintained for 30 seconds to 60 seconds.
D.F. within initial specified value
R_ins within initial specified value
The solder should cover over 95% of the critical
area of each termination
Test conditions for lead containing solder alloy
Temperature: 235 ±5 °C
Dipping time: 2 ±0.2 seconds
Depth of immersion: 10 mm
Alloy Composition: 60/40 Sn/Pb
Number of immersions: 1
Test conditions for leadfree containing solder alloy
Temperature: 245 ±5 °C
Dipping time: 3 ±0.3 seconds
Depth of immersion: 10 mm
Alloy Composition: SAC305
Number of immersions: 1
Feb 05, 2010 V.1