CS0603C0G104B6R3NRA Datasheet, PDF (9/14 Pages) SAMWHA ELECTRIC – Multi Layer Ceramic Capacitors

SAMWHA CAPACITOR Co., Ltd.
SMD Type
Reliability and Test Conditions(General Type)
No.
Item
Characteristic
Temperature
Compensating Type
High Dielectric Constant Type
Test Methods
and Conditions
1 Operating
Temperature Range
2 Insulation Resistance
3 Dielectric Strength
4 Capacitance
5 Dissipation Factor
C0G : 55 to 125
X7R : 55 to 125 X5R : 55 to 85
Y5V : 30 to 85
More than 10,000 or 500 (Whichever is smaller)
No defects or abnormalities
Within the specified tolerance
30 Min. :
Q 1,000 (DF 0.1%)
30 Max. :
Q 400 20C
(DF 1/(400 20C))
Char. 50V Min. 25V 16V 10V 6.3V
X7R 2.5%/ 3%/ 3.5%/ 5%/ 5%/
X5R 5% 7% 7% 10% 10%
Y5V
5%/
9%
7%/
9%
9% 12.5%/
12.5% 15%
15%
You can check the specification at
the appendix for each product
with mark
- Applied the rated voltage for 2
minutes of charging.
- The charge/discharge current is
less than 50mA.
- C0G : The rated voltage 300%
- X7R, X5R, Y5V :
250%
- Applied between the terminations
for 1 to 5 seconds.
- The charge/discharge current is
less than 50mA.
The capacitance/Q/D.F. should be
measured at 25 at the frequency
and voltage shown in the table.
Cap.
Testing
Frequency
C0G
1 0.1
(C 1000pF)
C0G
(C 1000pF)
1 0.1
X7R, X5R, Y5V
(C 10
1 0.1
6.3V Min.)
X7R, X5R, Y5V
(C 10 )
120 24
Testing
Voltage
0.5 to 5Vrms
1 0.2Vrms
1 0.2Vrms
0.5 0.1Vrms
6 Solderability of
Termination
Termination should be covered with more than
75% of new solder
- Pb-Free Type
Solder : 96.5Sn-3Ag-0.5Cu
Solder Temperature : 260 5
Immersion Time : 3 0.1sec
- Pre-Heating
at 80~120 for 10~30sec
7 _Resistance Appearance No marked defect
- Preheat the capacitor at 120 to 150
to
Soldering
Heat
Capacitchange Within 2.5% or 0.25
(whichever is larger)
Dissipation
Factor
(or Q)
30 Min. :
Q 1,000 (DF 0.1%)
30 Max. :
Q 400 20C
(DF 1/(400 20C))
X7R, X5R : 7.5%
Y5V : 20%
Char. 50V Min. 25V 16V 10V 6.3V
X7R 2.5%/ 3%/ 3.5%/ 5%/ 5%/
X5R 5% 7% 7% 10% 10%
Y5V
5%/
9%
7%/
9%
9% 12.5%/
12.5% 15%
15%
for 1 minute. (Preheating for 3225,
4520, 4532 Step1 : 100 to 120 , 1min
Step2 : 170 to 200 , 1min) Immerse the
capacitor in a eutectic solder solution
- Soldering Temp. : 260 5
- Immersion Time : 10 0.5sec
- Initial measurement
Perform a heat treatment at 150+0, -10
for one hour and then let sit for 48 4
hours at room temperature.
Perform the intial measurement.
- Measurement after test
Take it out and set it for 24 2 hours
(temperature compensating type)
I.R.
More than 10,000 or 500 (Whichever is smaller)
or 48 4 hours (high dielectric constant
type)then measure
Multi Layer Ceramic Capacitors