CS0603C0G104B6R3NRA Datasheet, PDF (10/14 Pages) SAMWHA ELECTRIC – Multi Layer Ceramic Capacitors

No.
Item
Characteristic
Temperature
Compensating Type
High Dielectric Constant Type
Test Methods
and Conditions
8 Temperature Appearance No marking defects
Cycle
Capacitance Within 2.5% or 0.25 X7R, X5R : Within 7.5%
Change
(whichever is larger) Y5V : Within 20%
Dissipation
Factor
(or Q)
30 Min. :
Q 1,000 (DF 0.1%)
30 Max. :
Q 400 20C
(DF 1/(400 20C))
Char. 50V Min. 25V 16V 10V 6.3V
X7R 5%/ 5%/ 5%/ 7.5%/ 7.5%/
X5R 7.5% 10% 10% 12.5% 12.5%
Y5V
7.5%/ 10%/ 12.5%
12.5% 12.5% 15%
15%/
20%
20%
I.R.
More than 10,000 or 500 (Whichever is smaller)
Perform the five cycless according
to the four heat treatments listed in
the following table.
Step 1
2
3
4
Min.
Temp. Operating
( ) Temp.
0, 3
Time
(Min) ^{30 3}
Room
Temp.
2 to 3
Max.
Operating Room
emp. Temp.
3, 0
30 3 2 to 3
- Initial measurement
Perform a heat treatment at 150+0,
-10 for one hour and then let sit
for 48 4 hours at room temperature.
- Measurement after test
Take it out and set it for 24 2 hours
(temperature compensating) or
48 4 hours(high dielectric constant
type) at room temperature, then
measure.
9 Humidity
Load
Appearance No marking defects
Capacitance
Change
Within 7.5% or 0.75
(whichever is larger)
X7R, X5R : Within 12.5%
Y5V : Within 30%, -40%
(Y5V/1.0 , 2.2 , 4.7 /10V)
Within 30% (others)
Dissipation
Factor
(or Q)
30 Min. :
Q 200 (DF 0.5%)
30 Max. :
Q 100 10/3C
(DF 1/(100 10/3C))
Char. 50V Min. 25V 16V 10V 6.3V
X7R 5%/ 5%/ 5%/ 7.5%/ 7.5%/
X5R 7.5% 10% 10% 12.5% 12.5%
Y5V
7.5%/ 10%/ 12.5%
12.5% 12.5% 15%
15%/
20%
20%
- Temperature : 40 2
- Humidity : 90~95%
- Hour : 500 12hrs
- Test Voltage : The rated voltage
- Take it out and set it for 24 2 hours
(temperature compensating) or
48 4 hours(high dielectric constant
type) at room temperature, then
measure.
The charge/discharge current is
less than 50mA
I.R.
More than 500 or 25 (Whichever is smaller)
10 ^High
Appearance
Temperature
Load
Capacitance
Change
Dissipation
Factor
(or Q)
No marking defects
Within 3% or 0.3
(whichever is larger)
X7R, X5R : Within 12.5%
Y5V : Within 30%(Cap. < 1.0
Within 30%, 40%
(Cap. 1.0
30 Min. :
Q 350 (DF 0.3%)
10 Cp 30
Q 275 +5/2C
(DF 1/(275+5/2C))
10 Max. :
Q 200+10C
(DF 1/(200+10C))
Char. 50V Min. 25V 16V 10V 6.3V
X7R 5%/ 5%/ 5%/ 7.5%/ 7.5%/
X5R 7.5% 10% 10% 12.5% 12.5%
Y5V
7.5%/ 10%/
12.5% 12.5%
12.5%
15%
15%/
20%
20%
- Testing time : 1000 12hrs
- Applied voltage :
Rated voltage < DC250V :
- Temperature :
C0G, X7R 125 3
X5R , Y5V 85 3
200%
- Measurement after test
Take it out and set it for 24 2
hours(temperature compensating
type)or 48 4 hours (high dielectric
constant type) at room temperature,
then measure.
The charge/discharge current is
less than 50mA.
I.R.
More than 10,000 or 50 (Whichever & Smaller)
SAMWHA CAPACITOR Co., Ltd.
SMD Type
No.
Item
11 Bending
Strength
Characteristic
Temperature
Compensating Type
High Dielectric Constant Type
Test Methods
and Conditions
- Substrate Material :
Glass EPOXY Board
- Board Thickness :
1.6mm
0.8mm(0603/1005size)
Test Condition
- Bending Limit : 1mm
- Pressurizing Speed : 1mm/sec
No cracking or marking defects shall occur
Capacitance Within 5% or 0.5
Change (whichever is larger)
X7R, X5R : Within 12.5%
Y5V : Within 30%
12 ^Vibration Appearance No defects or abnormalities
Resistance
Capacitance Whin the specified tolerance
Q/DF
30 Min. :
Q 1,000 (DF 0.1%)
30 Max. :
Q 400+20C
(DF 1/ (400+20C))
Char. 50V Min. 25V
X7R 2.5%/ 3%/
X5R 5% 7%
Y5V
5%/
9%
7%/
9%
16V 10V 6.3V
3.5%/ 5%/ 5%/
7% 10% 10%
9% 12.5%/
12.5% 15%
15%
Shown in Fig. After soldering and
then let sit for 24+4hr(temperature
compensating type), 48 4hr (high
dielectric constant type) at room
temperature.
The capacitor should be subjected
to a simple harmonic motion having
a total amplitude of 1.5mm, the
frequency being varied uniformly
between the approximate limits of
10 and 55Hz, shall be traversed(from
10Hz to 55Hz then 10Hz again) in
approximately 1 minute.
This motion shall be applied for a
period of 2 hours in each 3mutually
perpendicular directions(total is
6hours).
13 Humidity
Steady
State
Appearance No marking defects
Capacitance Within 5% or 0.5
Change (whichever is larger)
Dissipation
(or Q)
30 Min. :
Q 350 (DF 0.3%)
10 Cp 30
Q 275 +5/2C
(DF 1/(275+5/2C))
10 Max. :
Q 200+10C
(DF 1/(200+10C))
X7R, X5R : Within 12.5%
Y5V : Within 30%
Char. 50V Min. 25V 16V 10V 6.3V
X7R 5%/ 5%/ 5%/ 7.5%/ 7.5%/
X5R 7.5% 10% 10% 12.5% 12.5%
Y5V
7.5%/ 10%/ 12.5%
12.5% 12.5% 15%
15%/
20%
20%
- Temperature : 40 2
- Humidity : 90~95%
- Hour : 500 12hours
- Measurement after test
Take it out and set it for 24 2 hours
(temperature compensating type) or
48 4 hours(high dielectric constant
type) at room temperature, then
measure.
I.R
More than 1,000 or 50 (Whichever is Smaller)
Multi Layer Ceramic Capacitors