DEEFFSSeerireises(OSnlpyefcorifLicCaDtiBoancsklaignhdt ITnevesrtteMr eCtihrcoudits/ 6.3kVp-p) Specifications and Test Methods
Continued from the preceding page.
No.
Item
13
Soldering Effect
(On-Preheat)
Appearance
Capacitance
Change
Dielectric Strength
(Between Lead
Wires)
Appearance
Capacitance
Change
Q
Temperature
I.R.
14 and Immersion
Cycle
Dielectric Strength
(Between Lead
Wires)
Specifications
Test Method
No marked defect
Within ±2.5%
Per item 4.
First the capacitor should be
stored at 120+0/-5°C for
60+0/-5 sec.
Then, as in the figure, the lead
wires should be immersed in
solder of 260+0/-5°C up to 1.5 to
Thermal
,,^Capacitor
Scre_,,en_{,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,,M,,1too.l5t2e.n0mm}
Solder
2.0mm from the root of terminal
for 7.5+0/-1 sec.
Post-treatment: Capacitor should be stored for 1 to 2 hrs. at
room condition.*¹
No marked defect
The capacitor should be subjected to 5 temperature cycles,
then consecutively to 2 immersion cycles.
Within ±3%
<Temperature Cycle>
200+10C*²min. (10pF under)
275+5/2C*²min. (10pF min. and 30pF under)
350 min. (30pF min.)
Step Temperature (°C) Time (min)
1
-25±3
30
2
Room Temp.
3
2000MΩ min.
3
105±3
30
4
Room Temp.
3
<Immersion Cycle>
Cycle time: 5 cycles
Per item 4.
Step Temperature (°C) Time (min) Immersion Water
1
65+5/-0
15
Clean water
2
0±3
15
Salt water
Cycle time: 2 cycles
Post-treatment: Capacitor should be stored for 4 to 24 hrs. at
room condition.*¹
Appearance
No marked defect
15
Humidity (Under
Steady State)
Capacitance
Change
Q
Within ±5%
Set the capacitor for 500 +24/-0 hrs. at 40±2°C in 90 to 95%
relative humidity.
200+10C*²min. (10pF under)
Post-treatment: Capacitor should be stored for 1 to 2 hrs. at
275+5/2C*²min. (10pF min. and 30pF under)
room condition.*¹
350 min. (30pF min.)
I.R.
1000MΩ min.
16 Life
Appearance
Capacitance
Change
Q
I.R.
No marked defect
Apply 6.3kVp-p at the frequency in the Table for 1000+48/-0
hrs. at 105±2°C with a relative humidity of 50% max.
Within ±3%
(Charge/Discharge currentV50mA.)
<Frequency>
200+10C*²min. (10pF under)
275+5/2C*²min. (10pF min. and 30pF under)
350 min. (30pF min.)
Capacitance (pF)
to 10
12 to 22
Frequency (kHz)
100
45
27 to 47
33
2000MΩ min.
Post-treatment: Capacitor should be stored for 1 to 2 hrs. at
room condition.*¹
*¹ "Room condition" Temperature: 15 to 35°C, Relative humidity: 45 to 75%, Atmospheric pressure: 86 to 106kPa
*² "C" expresses nominal capacitance value (pF).
56