CSTCW24M0X53-R0 Datasheet, PDF (17/32 Pages) Murata Manufacturing Co., Ltd. – Ceramic Resonator

P17E.pdf
2012.10.31 ^{Note • Please read rating and CAUTION (for storage, operating, rating, soldering, mounting and handling) in this catalog to prevent smoking and/or burning, etc.}
• This catalog has only typical specifications because there is no space for detailed specifications. Therefore, please review our product specifications or consult the approval sheet for product specifications before ordering.
Specifications of CERALOCK^{® 3}
2. Mechanical and Environmental Specifications of CERALOCK^®
The tables show the standard test conditions of mechanical strength and
environmental specifications of CERALOCK^®.
Fig. 3-2 shows the changes of oscillation frequency in each test, the table on the
next page shows the criteria after the tests, and Fig. 3-3 shows the reflow
soldering profile.
˙Test Conditions for Standard Reliability of CERALOCK^®
Item
Conditions
1. Shock Resistance _{Measure after dropping from a height of a cm to b floor surface 3 times.}
3
2. Soldering
Heat Resistance
Lead terminals are immersed up to 2.0 mm from the resonator's body in solder bath of c , and then the resonator shall be
measured after being placed in natural condition for 1 hour.¹
Reflow profile show in Fig. 3-3 of heat stress is applied to the resonator, then the resonator shall be measured after being placed in
natural condition for 1 hour.²
3. Vibration Resistance Measure after applying vibration of 10 to 55Hz amplitude of 2 mm to each of 3 directions, X, Y, Z.
4. Humidity Resistance _{Keep in a chamber with a temperature of d and humidity of 90 to 95% for e hours. Leave for 1 hour before measurement.}
5. Storage at
High Temperature
Keep in a chamber at 85±2°C for e hours. Leave for 1 hour before measurement.
6. Storage at
Low Temperature
Keep in a chamber at f °C for e hours. Leave for 1 hour before measurement.
Keep in a chamber at -55°C for 30 minutes. After leaving at room temperature for 15 minutes, keep in a chamber at +85°C for 30
7. Temperature Cycling
minutes, and then room temperature for 15 minutes. After 10 cycles of the above, measure at room temperature.
8. Terminal Strength
Apply 1 kg of static load vertically to each terminal and measure.
∗1 Applies to CERALOCK^® Lead Type
∗2 Applies to MHz Band Chip CERALOCK^®
1. CSTLS Series
Type
fosc.
a
G
03.40—10.00MHz
100
X
16.00—50.00MHz
100
b
concrete
concrete
c
350±10°C
350±10°C
d
60±2°C
60±2°C
e
1000
1000
f
−55±2°C
−55±2°C
2. CSACW Series
Type
fosc.
a
b
c
X
20.01—50.00MHz
100
wooden plate
—
d
60±2°C
e
1000
f
−55±2°C
3. CSTCC/CSTCR/CSTCE/CSTCW Series
Type
fosc.
a
b
c
G
02.00—13.99MHz
100
wooden plate
—
V
14.00—20.00MHz
100
wooden plate
—
X
20.01—70.00MHz
100
wooden plate
—
d
60±2°C
60±2°C
60±2°C
e
1000
1000
1000
f
−55±2°C
−55±2°C
−55±2°C
15