DE2E3KY102MN2AM01 Datasheet, PDF (22/83 Pages) Murata Manufacturing Co., Ltd. – Safety Standard Certified Ceramic Capacitors/ High Voltage Ceramic Capacitors

!Note • Please read rating and !CAUTION (for storage, operating, rating, soldering, mounting and handling) in this catalog to prevent smoking and/or burning, etc.
C85E.pdf
• This catalog has only typical specifications because there is no space for detailed specifications. Therefore, please review our product specifications or consult the approval sheet for product specifications before ordering.
Jul.13,2011
DEJ Series S(WpehcicifhicMateioent sJaapnadnTeseestLMawet)hSopdescifications and Test Methods
Continued from the preceding page.
No.
Item
Specifications
Appearance No marked defect
Test Method
Capacitance
Change
Char.
E
F
Capacitance Change
Within ±20%
Within ±30%
16
Humidity
Loading
D.F.
Char.
E
F
Specifications
D.F.V5.0%
D.F.V7.5%
5
17 Life
I.R.
Dielectric
Strength
Appearance
1000MΩ min.
Per Item 6
No marked defect
Capacitance
Change
Char.
E
F
Capacitance Change
Within ±20%
Within ±30%
I.R.
1000MΩ min.
Dielectric
Strength
Per Item 6
18 Flame Test
The capacitor flame discontinued as follows.
Cycle
1 to 2
3
Time (sec.)
15 max.
60 max.
Apply the rated voltage for 500±12 hrs. at 40±2˚C in 90 to 95%
relative humidity.
Pre-treatment:
Capacitor should be stored at 85±2˚C for 1 hr., then placed at
room condition*¹ for 24±2 hrs. before initial measurements.
Post-treatment:
Capacitor should be stored for 1 to 2 hrs. at room condition.*¹
Apply a voltage from Table 2 for 1500 hrs. at 85±2˚C, relative
humidity 50% max.
<Table 2>
Applied Voltage
AC500V(r.m.s.), except that once each hour the voltage
is increased to AC1000V(r.m.s.) for 0.1 sec.
Pre-treatment:
Capacitor should be stored at 85±2˚C for 1 hr., then placed at
room condition*¹ for 24±2 hrs. before initial measurements.
Post-treatment:
Capacitor should be stored for 4 to 24 hrs. at room condition.*¹
The capacitor should be subjected
to applied flame for 15 sec. and then
removed for 15 sec. until 3 cycles
are completed.
Gas Burner: Inside Dia. 9.5
76
38
Capacitor
Flame
127
(in mm)
Robustness
19 of
Terminations
Tensile
Bending
Lead wire should not be cut off. Capacitor should
not be broken.
As shown in the figure at right, fix the body of the
capacitor, apply a tensile weight gradually to
each lead wire in the radial direction of the
capacitor up to 10N and keep it for 10±1 sec.
W
Each lead wire should be subjected to 5N of weight and bent
90° at the point of egress, in one direction, then returned to its
original position and bent 90° in the opposite direction at the
rate of one bend in 2 to 3 sec.
Appearance No marked defect
Capacitance
Change
Char.
E
F
Capacitance Change
Within ±20%
Within ±30%
Char.
Specifications
D.F.
E
D.F.V5.0%
F
D.F.V7.5%
The capacitor should be subjected to 5 temperature cycles,
then consecutively to 2 immersion cycles.
Step
1
2
3
4
<Temperature Cycle>
Temperature (ºC)
-25+0/-3
Room temp.
85+3/-0
Room temp.
Time (min)
30
3
30
3
Cycle time: 5 cycles
Temperature I.R.
20
and
Immersion
Cycle
1000MΩ min.
Dielectric
Strength
Per Item 6
Step
1
2
<Immersion Cycle>
Temperature (ºC)
65+5/-0
0±3
Time
(min)
15
15
Immersion
Water
Clean
water
Salt
water
Cycle time: 2 cycles
Pre-treatment:
Capacitor should be stored at 85±2˚C for 1 hr., then placed at
room condition*¹ for 24±2 hrs.
Post-treatment:
Capacitor should be stored for 4 to 24 hrs. at room condition.*¹
*¹ "Room condition" Temperature: 15 to 35°C, Relative humidity: 45 to 75%, Atmospheric pressure: 86 to 106kPa
20