V175LT5CP Datasheet, PDF (4/10 Pages) Littelfuse – Radial Lead Varistors > C-III series | |||
|
◁ |
Varistor Products
Radial Lead Varistors > C-III series
Current Energy and Power Dissipation Ratings
Should transients occur in rapid succession, the average
power dissipation is the energy (watt-seconds) per pulse
times the number of pulses per second. The power so
developed must be within the speciï¬cations shown on the
Device Ratings and Speciï¬cations Table for the speciï¬c
Figure 1A - Power Derating for Epoxy Coated
100
90
80
70
60
50
40
30
20
10
0
-55 50 60 70 80 90 100 110 120 130 140 150
AMBIENTTEMPERATURE ( oC)
Peak Pulse Current Test Waveform
device. The operating values of a MOV need to be derated
at high temperatures as shown above. Because varistors
only dissipate a relatively small amount of average power
they are not suitable for repetitive applications that involve
substantial amounts of average power dissipation.
Figure 1B - Power Derating for Phenolic Coated
100
90
80
70
60
50
40
30
20
10
0
-55 50 60 70 80 90 100 110 120 130 140 150
AMBIENTTEMPERATURE ( oC)
100
90
50
10
O1
Figure 2
T
T1
T2
TIME
01 = Virtual Origin of Wave
T = Time from 10% to 90% of Peak
T = Rise Time = 1.25 x T
1
T = Decay Time
2
Example - For an 8/20 μs Current Waveform:
8μs = T1 = Rise Time
20μs = T2 = Decay Time
Transient V-I Characteristics Curves
Pulse Rating Curves
Maximum Clamping Voltage for 10mm Parts
V130LA5C(P) â V625LA10C(P)
10000
MODEL SIZE = 10MM
TA = -55oC TO 85oC
130 to 625VM(AC) RATING
MAXIMUM CLAMP
VOLTAGE
510
550
625
460 440 420
300
320
385
230
250
275
1000
100
0.001
0.01
Figure 3
130 140 150 175
0.1
1
10
100
1000
10000
PEAK CURRENT (A)
Repetitive Surge Capability for 10mm Parts
V130LA5C(P)-V320LA10C(P)
10,000
1
2
15
1,000
102
103
100
â
MODEL SIZE = 10mm
TA = -55oC TO 85oC
104
105
106
10
1
10
Figure 4
100
1,000
SURGE IMPULSE DURATION (μs)
10,000
C-III Varistor Series
116
Revised: June 5, 2013
© 2013 Littelfuse, Inc.
Speciï¬cations are subject to change without notice.
Please refer to www.littelfuse.com/series/c-iii.html for current information.
|
▷ |