Solder Reflow Thermal Profile
300
PREHEATING RATE 3°C + 1°C/–0.5°C/SEC.
REFLOW HEATING RATE 2.5°C ± 0.5°C/SEC. PEAK
TEMP.
245°C
200
160°C
150°C
140°C
100
2.5°C ± 0.5°C/SEC.
3°C + 1°C/–0.5°C
PREHEATING TIME
150°C, 90 + 30 SEC.
30
SEC.
30
SEC.
PEAK
TEMP.
240°C
PEAK
TEMP.
230°C
SOLDERING
TIME
200°C
50 SEC.
ROOM
TEMPERATURE
0
0
TIGHT
TYPICAL
LOOSE
50
100
150
200
250
TIME (SECONDS)
Note: Non-halide flux should be used.
Regulatory Information
The HCPL-2602/2612 have been
approved by the following
organizations:
UL
Recognized under UL 1577,
Component Recognition Program,
File E55361.
CSA
Approved under CSA Component
Acceptance Notice #5, File CA
88324.
Recommended Pb-Free IR Profile
tp
Tp
260 +0/-5 °C
TL 217 °C
RAMP-UP
3 °C/SEC. MAX.
Tsmax 150 - 200 °C
Tsmin
ts
PREHEAT
tL
60 to 180 SEC.
TIME WITHIN 5 °C of ACTUAL
PEAK TEMPERATURE
20-40 SEC.
RAMP-DOWN
6 °C/SEC. MAX.
60 to 150 SEC.
25
t 25 °C to PEAK
TIME
NOTES:
THE TIME FROM 25 °C to PEAK TEMPERATURE = 8 MINUTES MAX.
Tsmax = 200 °C, Tsmin = 150 °C
Note: Non-halide flux should be used.
Insulation and Safety Related Specifications
Parameter
Symbol Value
Min. External Air Gap
(External Clearance)
L(I01)
7.1
Min. External Tracking
L(I02)
7.4
Path (External Creepage)
Min. Internal Plastic
0.08
Gap (Internal Clearance)
Tracking Resistance
(Comparative Tracking
Index)
Isolation Group
CTI
200
IIIa
Units
mm
mm
mm
V
Conditions
Measured from input terminals to output terminals,
shortest distance through air.
Measured from input terminals to output terminals,
shortest distance path along body.
Through insulation distance, conductor to conductor,
usually the direct distance between the photoemitter
and photodetector inside the optocoupler cavity.
DIN IEC 112/VDE 0303 Part 1
Material Group (DIN VDE 0110, 1/89, Table 1)
Option 300 - surface mount classification is Class A in accordance with CECC 00802.
5