CC0603ZRY5V9BB104 Datasheet, PDF (12/14 Pages) YAGEO Corporation – SURFACE-MOUNT CERAMIC MULTILAYER CAPACITORS

Product specification 12
Surface-Mount Ceramic Multilayer Capacitors ^{General Purpose & High Cap.}
Y5V
14
6.3 V to 50 V
TEST
Rapid change
of
temperature
TEST METHOD
IEC 60384- 4.11
21/22
PROCEDURE
Preconditioning;
150 +0/–10 °C for 1 hour, then keep for
24 ±1 hours at room temperature
5 cycles with following detail:
30 minutes at lower category temperature
30 minutes at upper category temperature
Recovery time 24 ±2 hours
REQUIREMENTS
No visual damage
<General purpose series>
∆C/C
Class2:
Y5V: ±20%
<High Capacitance series>
∆C/C
Class2:
Y5V: ±20%
D.F. meet initial specified value
R_ins meet initial specified value
Damp heat
with U_r load
4.13 _{1. Preconditioning, class 2 only:}
No visual damage after recovery
150 +0/-10 °C /1 hour, then keep for
24 ±1 hour at room temp
<General purpose series>
2. Initial measure:
∆C/C
Spec: refer initial spec C, D, IR
Class2:
3. Damp heat test:
Y5V: ±30%
500 ±12 hours at 40 ±2 °C;
D.F.
90 to 95% R.H. 1.0 U_r applied
Class2:
4. Recovery:
Y5V: ≤ 15%
Class 2: 24 ±2 hours
5. Final measure: C, D, IR
R_ins
Class2:
P.S. If the capacitance value is less than the
Y5V: ≥ 500 MΩ or R_ins x C_r ≥ 25s
whichever is less
minimum value permitted, then after the other
measurements have been made the capacitor shall
be precondition according to “IEC 60384 4.1” and
then the requirement shall be met.
<High Capacitance series>
∆C/C
Class2:
Y5V: ±30%
D.F.
Class2:
Y5V: 2 x initial value max
R_ins
Class2:
Y5V: 500 MΩ or R_ins x C_r ≥ 25s
whichever is less
Jul 29, 2010 V.5
www.yageo.com