82380180121 Datasheet, PDF (5/5 Pages) Wurth Elektronik GmbH & Co. KG, Germany. – 0612 ESD ARRAY 4 VARISTOR

Spezifikation für Freigabe / specification for release
Kunde / customer :
Artikelnummer / part number :
82.380.180.121
Bezeichnung :
description :
0612 ESD ARRAY 4 VARISTOR
SMD size: 0612
E Testbedingungen / test conditions :
BASIC TEST
Characteristics
Standard Test Condition
Max. Working Voltage
Varistor Voltage
Max. Clamping Voltage
Test Method/Description
Environmental condition under which every measuring is done without doubt on the measuring results.
Unless specially specified, temperature, relative humidity are 5 to 35℃, 45 to 85﹪RH.
Maximum steady-state DC operating voltage the device can maintain and typical leakage current at 25℃
not exceed 50 µA.
With the specified measuring current of 1mA DC applied.
Maximum peak voltage across the TVS measured at a specified pulse current（A）and waveform 8/20µs.
Surge Current
Surge Shift △V/V
Energy Absorption
Typical Capacitance
Leakage Current
Maximum peak current which may be applied with the specified waveform 8/20µs without device failure.
The shift of TVS voltage after suffering the specified surge current.
Maximum energy which may be dissipated with a specified waveform 10/1000µs.without device failure.
Device Capacitance measured with zero voltage bias 0.5VRMS and 1KHZ
Typical leakage current at 25℃＜50µA
ENVIRONMENTAL RELIABILITY TEST
Characteristic
Test method and description
The specimen shall be subjected to 150 ± 2℃ for 1000 ± 12 hours in a thermostatic bath without load and
High Temperature Storage
then stored at room temperature and humidity for 1 to 2 hours. The change of varistor voltage shall be
within 10 ﹪.
The temperature cycle of specified temperature shall be repeated five times and then stored at room
Temperature Cycle
temperature and humidity for one or two hours. the change of varistor voltage shall be within 10 ﹪and
mechanical damage shall be examined.
Step
Temperature Period
1
-40±3℃
30Min±3
Room
2
Temperature 1~2 hours
3
8R5o±o2m℃
30Min±3
4
Temperature 1~2 hours
After being continuously applied the maximum allowable voltage at 85 ± 2℃ for 1000± 2 hours, the
High Temperature Load
specimen shall be stored at room temperature and humidity for one or two hours, the change of varistor
voltage shall be within 10﹪.
The specimen should be subjected to 40 ± 2℃, 90 to 95 ﹪RH environment , and the maximum allowable
Damp Heat Load/Humidity Load
voltage applied for 1000 hours, then stored at room temperature and humidity for one or two hours. the
change of varistor voltage shall be within 10﹪
Low Temperature Storage
The specimen should be subjected to 40 ± 2℃, without load for 1000 hours and then stored at room
temperature for one or two hours. the change of varistor voltage shall be within 10 ﹪
Freigabe erteilt /
general release:
Kunde / customer
Datum / date
Unterschrift / signature
Würth Elektronik
Geprüft / checked
2006-06-02 Kontrolliert / approved
JP. Penlou
JP. PENLOU
JP. PENLOU
JP. PENLOU
JP. PENLOU
Name
High Temperature Load
New P/N
Operating temp. Range
Lead free soldering
Änderung / modification
Würth Elektronik eiSos GmbH & Co.KG - Radialex department
D-74638 Waldenburg · Max-Eyth-Straße 1 - 3 · Germany · Telefon (+49) (0) 7942 - 945 - 0 · Telefax (+49) (0) 7942 - 945 - 400
http://www.we-online.com
06-07-31
2006-06-02
2005-11-30
2005-11-04
Datum / date
PAGE/SEITE 5 - TO/VON 5