CDB455C4 Datasheet, PDF (2/3 Pages) Shoulder Electronics Limited. – This specification is applicable to ceramic discriminator CDB455C4 use for SANYO IC LA8610. | |||
|
◁ |
1. Application
This specification is applicable to ceramic discriminator CDB455C4 use for SANYO IC
LA8610.
2. Electrical Characteristics
This discriminator must need following performance.
2-1) Anti-resonate frequency (Fa) : 470±1.5 kHz.
2-2) Resonant Impedance (Ri) : 300 ΩMax.
2-3) ÎF(Fa-Fr)
: 43±2.0 kHz.
Fr: resonant frequency
2-4) Capacitance (at 1 kHz)
: 140 pF±20%.
3. Environmental Test
3-1) Temperature Characteristics
At the temperature range of 25±5â,the discriminators shall meet the electrical properties
in item 2-1~2-4,and at â20~+80â the Anti-resonant frequency shall not very more than
±2.0 kHz.
3-2) Vibration
The discriminators shall suffer no mechanical damage and meet the 2-1~2-4 electrical
Characteristics after being vibrated with a sine wave motion having an amplitude of 1.0
mm from 10 to 55KHz per 1 minute, applied for 30 minutes in three different directions
(x,y,z).
3-3) Humidity
The discriminators shall be place in a humidity chamber at 90~95% relative
humidity and 40~45â for a period of minimum 8 hours. The discriminators shall be left
for the period of more than 24 hours at the room temperature after its removal from the
humidity chamber.The discriminators shall meet the 2-1~2-4 electrical characteristics and
the appearance of discriminators is to be normal.
3-4) Dropped Shock
The discriminators shall suffer no mechanical damage and meet the 2-1~2-4
electrical characteristics outlined on this specification after being dropped 3 times to
concrete floor from the 30 cm height.
3-5) Solder ability
The terminal surface shall be covered over 3/4 by the solder after dipped the leads
into 230±5â solder pot containing (Sn 63% Pb 37%) molten alloy for 3±1 seconds.
3-6) Soldering Heat-Resistance
The discriminators shall be assembled to the 1 mm âthrough-holeâ P.C. bored and placed in
solder solution (Sn63% Pb37%) at 250±10â for duration of 3±1 seconds. After removal
from the solder solution chamber, the discriminators may be cleaned with chlorothene and
left for more then 24 hours at the room temperature. The discriminators shall meet the
2-1~2-4 electrical characteristics are to be normal.
3-7) Lead Strength
The discriminators shall suffer no mechanical damage and meet the 2-1~2-4 electrical
characteristics outlined on this specification after static load of 1.0 kg for 1 minute is
applied in the direction of the insertion side.
3-8) Temperature
The discriminators shall be held at each cycle consist of three temperature
Http://www.shoulder.cn