CL10B101KB8NNNC Datasheet, PDF (24/35 Pages) Samsung semiconductor – Multilayer Ceramic Capacitor

Multilayer Ceramic Capacitor - General
NO
ITEM
PERFORMANCE
TEST CONDITION
MORE THAN 75% OF THE TERMINAL
SOLDER TEMPERATURE : 230±5℃
SURFACE IS TO BE SOLDERED NEWLY, DIP TIME : 3±1 Sec
SO METAL PART DOES NOT COME
SOLDER : H63A
OUT OR DISSOLVE
FLUX
: RMA TYPE
*PB-FREE
11
SOLDERABILITY
SOLDER TEMPERATURE : 260±5℃
SOLDER : Sn96.5-3Ag-0.5Cu
IN PB--FREE PART, MORE THAN 95%
OF THE TERMINAL SURFACE IS TO BE
SOLDERED NEWLY
Flux : RMA TYPE
DIP TIME : 3±0.1Sec
* PRE-HEATING : AT 80~120℃ FOR
10~30SEC.
APPEARANCE
CAPACITANCE
NO MECHANICAL DAMAGE
SHALL OCCUR
CHARACTERISTIC
CAP. CHANGE
WITHIN ±2.5% OR
CLASSⅠ
±0.25㎊ WHICHEVER
IS LARGER
DIP : SOLDER TEMPERATURE OF
270±5℃
DIP TIME :10±1 SEC.
EACH TERMINATION SHALL BE FULLY
IMMERSED AND PREHEATED
AS FOLLOWING:
RESISTANCE
TO
12
SOLDERING
HEAT
Q
CLASS Ⅰ
Tanδ
CLASS Ⅱ
INSULATION
RESISTANCE
CLASSⅡ
A,B WITHIN ±7.5%
F WITHIN ±20%
30㎊ AND OVER : Q≥ 1000
LESS THAN 30㎊ : Q≥ 400+20×C
TO SATISFY THE SPECIFIED
INITIAL VALUE
TO SATISFY THE SPECIFIED
INITIAL VALUE
STEP TEMP.(℃)
1
80~100
2
150~180
TIME
(SEC.)
60
60
MEASURE AT ROOM TEMP. AFTER
COOLING FOR
CLASSⅠ : 24 ± 2 HOURS
CLASSⅡ : 48 ± 4 HOURS
WITHSTANDING TO SATISFY THE SPECIFIED
VOLTAGE
INITIAL VALUE
VIBRATION
13
TEST
APPEARANCE
CAPACITANCE
Q
CLASS Ⅰ
Tanδ
CLASS Ⅱ
NO MECHANICAL DAMAGE SHALL
OCCUR.
CHARACTERISTIC
CAP. CHANGE
CLASS Ⅰ
WITHIN ±2.5% OR
±0.25㎊
WHICHEVER
IS LARGER
CLASS
Ⅱ
A,B WITHIN ±5%
F WITHIN ±20%
30㎊ AND OVER : Q≥ 1000
LESS THAN 30㎊ : Q≥ 400+20×C
TO SATISFY THE SPECIFIED
INITIAL VALUE
BENDING SHALL BE APPLIED TO
THE LIMIT(1mm) WITH 0.3mm/SEC.
KEEP THE TEST BOARD AT THE LIMIT
POINT IN 5 SEC., THEN MEASURE
CAPACITANCE.
CHAR. FREQUENCY RANGE
A,B,C,F 10Hz → 55Hz → 10Hz
CHAR.
A,B,C,F
TRAVERSED TIME
1 min
THE ENTIRE FREQUENCY RANGE, FROM 10
TO 55Hz AND RETURN TO 10Hz, SHALL BE
TRAVERSED IN 1 MINUTE.
INSULATION
RESISTANCE
TO SATISFY THE SPECIFIED
INITIAL VALUE
THIS CYCLE SHALL BE PERFORMED 2
HOURS IN EACH THERE MUTUALLY
PERPENDICULAR DIRECTION,
FOR TOTAL PERIOD OF 6 HOURS.
* THE INITIAL VALUE OF HIGH DIELECTRIC CONSTANT SERIES SHALL BE MEASURED
AFTER THE HEAT TREATMENT OF 150 +0/-10℃, 1Hr AND SITTING OF 48±4hr AT ROOM TEMPERATURE & ROOM HUMIDITY.
- 23 -