MA1206XR104K500R Datasheet, PDF (1/2 Pages) RFE international – CERAMIC CAPACITORS MA Series: Multilayer Surface Mount

CERAMIC CAPACITORS
RoHS
MA Series: Multilayer Surface Mount ^ü
INTRODUCTION
FEATURES
Multilayer chip capacitors are ideal for
•Miniature Size
applications That require a large
•High Mounting Density
capacitance to size ratio. The Nickel
•Nickel Barrier Termination
barrier termination prevents
L
•High voltages are available
W
excessive leaching during wave
up to 3000 volts.
(reflow) or dip (flow)soldering.
•RoHS Compliant
T
DIMENSIONS
Size
LXW IN
MM
T (max) IN
MM
0402
0.04 x 0.02
1.00 x 0.50
0.022
0.55
0603
0.063 x 0.03
1.60 x 0.80
0.036
0.92
0805
0.08 x 0.05
2.03 x 1.27
0.053
1.35
1206
0.125 x 0.06
3.18 x 1.60
0.073
1.85
1210
0.125 x 0.100
3.18 x 2.54
0.106
2.7
1812
0.180 x 0.125
4.50 x 3.20
0.106
2.7
*Thicknesses noted are maximum. Thicknesses are less on low capacitance values. _{Terminations (Nickel Barrier)}
2220
0.224 x 0.197
5.7 x 5.0
0.106
2.7
SPECIFICATIONS
Ceramic Body
Specification
COG(NPO)
Temp(°C)
-55~ +125
TempCoeff
0% ±30PPM
Dissipation (25°C) <0.001@1KHz
Insulation Resistance >1000M F or 100G
X7R/X5R
-55~ +125/-55~ +85
0±15%
<0.025@1KHz
>1000M F or 100G
Y5V
-30~ +85
C%+22 to -82%
<0.025@1KHz
>500M F or 10,000M
Electrodes
Silver Metalization
Nickel Barrier Layer
Solder Plated
COG/NPO: Typical Capacitance Change vs. Temperature
15%
Typical Capacitance Change
10%
Envelope: 0 ± 30 ppm/°C
5%
X5R: Typical Capacitance Change vs. Temperature
15%
10%
0.5%
0%
0%
-5%
-5%
-10%
-10%
-15%
-55°C
-25°C
0°C
25°C
50°C
75°C
100°C
125°C
-15%
-55°C
-25°C
0°C
25°C
50°C
75°C
100°C
125°C
X7R: Typical Capacitance Change vs. Temperature
15%
10%
5%
0%
-5%
-10%
-15%
-55°C
-25°C
0°C
25°C
50°C
75°C
100°C
125°C
Y5V: Typical Capacitance Change vs. Temperature
40%
20%
0%
-20%
-40%
-60%
80%
-100%
-55°C
-25°C
0°C
25°C
50°C
75°C
100°C
125°C
PART NUMBER EXAMPLE
MA 1206 XR 104 K 500 R
*Surface mount offerings continue to change, please contact RFE International, for values, sizes, and voltages not listed.
RFE International • Tel:[phone] • Fax:[phone] • E-Mail [e-mail]
C1BC01
REV2006.10.02