QCB Datasheet, PDF (1/1 Pages) Qualtek Electronics Corporation – MOLDED PARTS

MOLDED PARTS
QCB
HEAT SHRINKABLE CONDUCTIVE BREAKOUT
UP TO 36kV
Features/Applications
The conductive breakouts are made from radiation cross-linked
polyolefin. The electrically semi-conductive of the breakout
provides effective conductive screen and sealing protection to
the cable terminations. The breakout can be used for cable
terminations up to 36kV.
Operating temperature: -55°C to +105°C
Minimum shrink temperature: 110°C
Full Recovery Temperature: 130°C
Standard color: Black
RoHS Compliant
Qualtek Electronics
Technical Data
Property
Operating Temperature
Tensile Strength
Tensile Strength After Thermal Aging (120°C, 168 hrs.)
Elongation at Break
Elongation at Break After Thermal Aging (120°C, 168 hrs.)
Water Absorption
Volume Resistance
Test Method
IEC 216
ASTM D 2671
ASTM D 2671
ASTM D 2671
ASTM D 2671
ISO 62
IEC 93
Typical Data
-55°C to +105°C
12 MPa min.
10 MPa min.
250% min.
200% min.
1% max.
10 ⁴ Ω.cm (max.)
Product Dimensions
Part
Number
D (mm)
a (Min.)
b (Max.)
QCB320-60/24
60
24
QCB330-80/38
80
38
QCB340-110/50
110
50
QCB350-125/57
125
57
QCB360-140/70
140
70
Notes:
(a) as supplied
(b) after recovery
l (mm)
a (Min.)
25
35
46
55
62
b (Max.)
8
11
17.5
20
26
Recovered Length
± 10%
L (mm)
F (mm)
183
45
215
57
250
65
260
57
280
70
Recovered Wall
± 10%
Dw (mm) lw (mm)
3.0
2.5
4.0
4.0
4.0
4.0
4.0
4.0
4.0
4.0
ISO-9001 Company
www.qualtekusa.com
QCB-200C