QAS Datasheet, PDF (1/1 Pages) Qualtek Electronics Corporation – MOLDED PARTS

MOLDED PARTS
QAS
HEAT SHRINKABLE , ANTI-TRACKING RAIN SHIELDS, UP TO 36kV
SHRINK RATIO 2:1
Features/Applications
QAS is made from high creep resistance, anti-tracking polyolefin
compound and coated with anti-track, weather resistant mastic. The
high creep resistance and anti-tracking properties of the products
provide maximum operation reliability. Used to provide insulation
protection for cable outdoor termination.
Operating temperature: -55°C to +105°C
Minimum shrink temperature: 110°C
Standard color: Red
RoHS Compliant
Qualtek Electronics
Technical Data
Property
Tensile Strength
Elongation at Break
Tensile Strength After Aging (120°C, 168 hrs.)
Elongation at Break After Aging (120°C, 168 hrs.)
Dielectric Strength
Tracking Resistance (3.75KV, 1hr. )
Electric Constant
Volume Resistance
Flammability (Oxygen Index)
Copper Corrosion (120°C, 168 hrs.)
Cold Bend (-40°C, 4hrs.)
Test Method
ASTM D 2671
ASTM D 2671
ASTM D 2671
ASTM D 2671
ASTM D 2671
ASTM D 2303
IEC 250
ASTM D 2303
IEC 93
ASTM D 2671
ASTM D 2671
Product Dimensions
Size
(mm)
As Supplied (mm)
D2 (Min.)
After Recovered (mm)
D2 (Max.)
D1 (Nom.)
35/12
35
12
95
48/20
48
20
120
60/20
60
20
120
60/30
60
30
140
75/30
75
30
140
100/35
100
35
140
120/45
120
45
200
Notes:
1. * See Part Number Guide for standard packaging codes.
2. Special sizes, packaging, colors and cut pieces are available upon request.
Typical Data
>13 MPa
> 400%
10.4 MPa
350%
15kV / mm
Pass
3.0
10¹⁴ Ω.cm
25
no corrosion
no cracking
H (Min.)
18
21
21
25
25
35
35
W (± 10%)
3.0
3.0
3.0
3.0
3.0
3.0
3.0
ISO-9001 Company
www.qualtekusa.com
QAS-200C