HHR70AAAJ Datasheet, PDF (1/1 Pages) Panasonic Battery Group – NICKEL METAL HYDRIDE BATTERIES | |||
|
NICKEL METAL HYDRIDE BATTERIES: INDIVIDUAL DATA SHEET
HHR70AAAJ Cylindrical HR AAA size (HR 11/45)
Dimensions (with Tube)
(mm)
10.5
+-
0
0.7
(+)
Typical Charge Characteristics
2.0
Charge: 1It(650mA) x 1.2h at 0.20, 45ËC
Rest:
1~3h
1.8
Discharge: 1It(650mA) to 1.0V at 20ËC
1.6
1.4
1.2
1.0
0.8
0
0ËC
20ËC
45ËC
100 200 300 400 500 600 700 800 900 10001100 1200
Discharge Time (minutes)
44.5
+-
0
1.0
()
Specifications
Diameter
Height
Approximate
Weight
mm
10.5+0/-0.7
44.5+0/-1.0
Grams
13
inch
0.41+0/-0.03
1.75+0/-0.04
Ounces
0.46
Nominal Voltage
1.2V
Discharge
Capacity*
Average**
Rated (Min.)
Approx. Internal impedance
at 1000Hz at charged state.
Charge
Standard
Rapid
Charge Standard
Rapid
Discharge
Storage
< 1 year
< 3 months
< 1 month
720 mAh
700 mAh
30mâ¦
70mA (0.1It) x 16hrs.
650mA (1It) x 1.2 hrs.
ËC
0ËC to 45ËC
ËF
32ËF to 113ËF
0ËC to 40ËC 32ËF to 104ËF
-10ËC to 65ËC 14ËF to 149ËF
-20ËC to 35ËC -4ËF to 95ËF
-20ËC to 45ËC -4ËF to 113ËF
-20ËC to 55ËC -4ËF to 131ËF
* After charging at 0.1It for 16 hours, discharging at 0.2It.
** For reference only.
Battery performance and cycle life are strongly affected by how they
are used. In order to maximize battery safety, please consult Panasonic
when determining charge / discharge specs, warning label contents
and unit design.
Typical Discharge Characteristics
2.0
Charge: 1It(650mA) x 1.2h at 20ËC
Rest:
1h
1.8
Discharge: 0.2It(130mA) to 1.0V at 20ËC
1.6
1.4
1.2
1.0
0.8
0 100 200 300 400 500 600 700 800 900 1000 1100 1200
Discharge Time (minutes)
2.0
Charge: 1It(650mA) x 1.2h at 20ËC
Rest:
1 ~ 5h
1.8
Discharge: 1It(650mA) to 1.0V at 20ËC
1.6
1.4
1.2
1.0
0.8
0 100 200 300 400 500 600 700 800 900 1000 11001200
Discharge Time (minutes)
Note:
[It] was previously expressed as [C]. [It] is an IEC standard expression
for the amount of charge or discharge current and is expressed as:
It(A) = Cn (Ah)/1h.
⢠[It] is the reference test current in ampres
⢠[Cn] is the rated capacity of the cell or battery in Ampere-hours.
n = the time base [hours] for which the rated capacity is declared
NICKEL METAL HYDRIDE HANDBOOK
AUGUST 2005
This information is generally descriptive only and is not intended to make or imply any representation, guarantee or warranty with respect to any cells and batteries. Cell and battery designs/specifications are subject to
modification without notice. Contact Panasonic for the latest information.
|