152MWS402KG_13 Datasheet, PDF (1/4 Pages) Illinois Capacitor, Inc. – Metallized Polyester Film Capacitors for High Voltage Applications

MWS Metallized Polyester
Film Capacitors for High
Voltage Applications
• High Voltage
• Voltage Multipliers
Operating Temperature Range
Capacitance Tolerance
VDC
Rated Voltage
VAC
Dissipation Factor
(max) at 20˚C.
Insulation Resistance
@20˚C(<70% RH)
for 1 minute at 100VDC
Load Life Test
Damp Heat Test
Self inductance
Capacitance drift
Temperature Coefficient
Dielectric Strength
Dielectric
Electrodes
Construction
Leads
Coating
-55˚C to +105˚C
2500
500
4000
750
6300
1000
+/- 10% at 1kHz, 20˚C
10000
1200
For T>85°C the rated voltage must be decreased by 1.25% per °C
Freq (kHz)
C≤0.1µF
C>0.1µF
1
0.8%
0.8%
10
1.5%
1.5%
100
3.0%
≥100,000MΩ
2000 hours at 125% of rated voltage and at 85°C
Capacitance change
≤5% change from initial value.
Dissipation Factor
≤0.003 at 10kHz and 25°C
Insulation Resistance
≥50% of minimum specification
56 days at +40°C+/-2°C with 93%+/-2% relative humidity
Capacitance change
Dissipation Factor
Insulation Resistance
≤5% change from initial value.
≤0.005 at 1kHz and 25°C
≥50% of minimum specification
<1nH/mm of body length and lead wire length.
<1.0% up to 40°C after 2 years
+400ppm/˚C +/- 200ppm/˚C
160% of rated voltage for 2 seconds at 250°C applied between terminals
Polyester
Vacuum deposited metal layers
Extended metallized carrier film, internal series connections.
Tinned copper wire
Flame retardant polyester tape wrap (UL510)
with epoxy end seals (UL94V-0)
®
128