E30-3C81-E100 Datasheet, PDF (3/7 Pages) Ferroxcube International Holding B.V. – E cores and accessories | |||
|
◁ |
Ferroxcube
E cores and accessories
E30/15/7
GRADE
3F3
3F35
AL
(nH)
100 ±5%(1)
160 ±5%
250 ±5%
315 ±5%
400 ±8%
630 ±15%
1600 ±25%
1250 ±25%
µe
â 89
â142
â 222
â 280
â 355
â 560
â1 420
â1110
TOTAL AIR GAP
(µm)
â 1100
â 580
â 330
â 240
â 180
â 100
â0
â0
TYPE NUMBER
E30/15/7-3F3-E100
E30/15/7-3F3-A160
E30/15/7-3F3-A250
E30/15/7-3F3-A315
E30/15/7-3F3-A400
E30/15/7-3F3-A630
E30/15/7-3F3
E30/15/7-3F35
Note
1. Measured in combination with an equal gapped core half, clamping force for AL measurements, 20 ±10 N.
Core halves of high permeability grades
Clamping force for AL measurements 20 ±10 N.
GRADE
AL
(nH)
µe
3C11
3300 ±25%
â 2930
3E27
4100 ±25%
â 3640
AIR GAP
(µm)
â0
â0
TYPE NUMBER
E30/15/7-3C11
E30/15/7-3E27
Properties of core sets under power conditions
B (mT) at
GRADE
3C81
3C90
3C91
3C92
3C94
3C96
3F3
3F35
H = 250 A/m;
f = 25 kHz;
T = 100 °C
â¥320
â¥330
â¥320
â¥370
â¥330
â¥340
â¥320
â¥300
f = 25 kHz;
BË = 200 mT;
T = 100 °C
⤠0.82
⤠0.45
â
â
â
â
â
â
CORE LOSS (W) at
f = 100 kHz;
BË = 100 mT;
T = 100 °C
â
⤠0.48
⤠0.27(1)
⤠0.36
⤠0.36
⤠0.27
⤠0.47
â
f = 100 kHz;
BË = 200 mT;
T = 100 °C
â
â
⤠1.6(1)
⤠2.0
⤠2.0
⤠1.6
â
â
Properties of core sets under power conditions (continued)
B (mT) at
CORE LOSS (W) at
GRADE
3C96
3F3
3F35
H = 250 A/m;
f = 25 kHz;
T = 100 °C
â¥340
â¥320
â¥300
f = 500 kHz;
BË = 50 mT;
T = 100 °C
⤠1.5
â
⤠0.54
f = 500 kHz;
BË = 100 mT;
T = 100 °C
â
â
⤠4.2
f = 1 MHz;
BË = 30 mT;
T = 100 °C
â
â
â
Note
1. Measured at 60 °C.
2008 Sep 01
389
f = 400 kHz;
BË = 50 mT;
T = 100 °C
â
â
â
â
â
â
⤠0.80
â
f = 3 MHz;
BË = 10 mT;
T = 100 °C
â
â
â
|
▷ |