U0603C102JCT Datasheet, PDF (7/19 Pages) List of Unclassifed Manufacturers – Multilayer Ceramic Capacitors

Nickel Barrier
Multilayer Ceramic Capacitors
Item
Performance
Vibration
External
Appearance
Without distinct Damage
Capacitance
Change
(∆ C/C)
NPO: ±2.5% or ±0.25 pF maximum
(Whichever is larger)
X7R/X5R: ±7.5%
Y5V, Z5U: ±20%
NPO: C ≥30pF : Q ≥ 1000
C<30pF:Q ≥ 400 + 20°C
PS: C : Nominal capacitance (pF)
X7R, X5R, Y5V, Z5U : (Maximum Value)
DF or Q
T.C.
X7R/
X5R
Z5U
≥
50V
25V
16V ≤10V
2.5% 3.0% 3.5% 5.0%
4.0% -
-
-
Y5V 5.0% 7.5% 9.0% 12.5%
External
Appearance
No mechanical Damage
Deflection
Bending
Strength
Capacitance
Change
(∆ C/C)
Flexure ≥ 1mm
NPO: ±5% or ±0.5 pF maximum
(Whichever is larger)
X7R/X5R: ±12.5%
Y5V: ±30%
Test or Inspection Method
(Not apply for 0402 product)
Solder the capacitors to the test jig as shown in figure below
with IR-Reflow method. The capacitor shall be subjected to a
simple harmonic motion with the entire frequency range, from
10 to 55 Hz and return to 10 Hz ,shall be transverse in 1 min.
Amplitude (total excursion): 1.5mm
Amplitude tolerance: ± 15%
This motion shall be applied for a period of 2
hours in each of 3 mutually perpendicular
directions (a total of 6 hours)
External
Appearance
No mechanical Damage
Capacitance
Change
(∆ C/C)
DF
NPO: ±2.5% or ±0.25 pF maximum
(Whichever is larger)
X7R/X5R: ±7.5%
Y5V: ±20%
NPO: C ≥30pF : Q ≥ 1000
C<30pF: Q ≥ 400 + 20°C
Temperature
Cycle
X7R, X5R, Y5V and Z5U (Maximum value)
T.C.
X7R/
X5R
≥
50V
25V
16V ≤10V
2.5% 3.0% 3.5% 5.0%
(Not apply for 0402 product)
The capacitor shall be subject 5 cycles according to four heat
treatments listed in the following table.
Then leave the capacitors in ambient condition for the
following time before measurement.
Class II: 2~24 hours
Step
Temperature (°C)
Duration
(Minutes)
1 Minimum Operation Temperature ±3 30 ±3
2
Room Temperature (25°C)
2~5
3 Minimum Operation Temperature ±3 30 ±3
4
Room Temperature (25°C)
2~5
Z5U 4.0% -
-
-
Y5V 5.0% 7.5% 9.0% 12.5% ^{Preconditioning: (only for class 2):}
Perform a heat treatment at 150+0-10°C for one hour and
IR
1000MΩ minimum or 50Ω *F
(Whichever is smaller)
then let sit for 24 ±2 hours at room temperature.
Perform initial measurement.
Page 7
27/04/06 V1.0