HS407 Datasheet, PDF (1/2 Pages) List of Unclassifed Manufacturers – Heatshrink Adhesive Lined

Heatshrink
Adhesive Lined
Description:
This is a flexible, flame retarded heat-shrinkable polyolefin tubing, with
a shrink ratio of 4 : 1 with a thick wall adhesive which melts and flows,
to seal components contained within. Recommended for applications
requiring water-proofing for light cable and wire harnesses and protection
of connector components.
Features :
•  EPA method 3050B
: 1996 other acid digestion
•  BSEN1122
: 2001 method B other acid digestion
•  EPA method 3052B
: 1996 other acid digestion
•  EPA method 3060 and EPA 7196A
: 1992
•  Atomic absorption spectrometer / inductively coupled plasma atomic emission spectrometer (ICP + AES) UV-VIS
spectrophotometer
Characteristics:
Operating Temperature
: -55°C to +125°C
Minimum Shrink Temperature : 70°C
Shrink Ratio
: 3:1 and 4:1
Standard Colour
: Black
(Other colours are also available on request)
Applications:
Manufactured by co-extrusion of polyolefin and hot-melt adhesive. Designed to provide both insulation and sealing for the
protected items. Typically uses are the protection of automotive wires, bundled wires and metal tubes against water and
moisture. The high expansion ratio makes it possible to repair most damaged cable jackets without removing connectors.
Technical Data:
Property
Tensile Strength
Ultimate Elongation (%)
Longitudinal Shrinkage (%)
Heat Aging
Ultimate Elongation (%)
Flammability
Dielectric Strength (kv / mm)
Volume Resistivity (ohm-cm)
Copper Stability
Corrosion
Test Method
ASTM D 2671
UL 224
158°, 168hr
VW-1
IEC 243
UL224
ASTM D 2671
UL224
Typical Data
10.4Mpa
30
0 to -10
200
Pass (outer jacket only)
20
1 × 1014
Pass
No corrosion