SH Datasheet, PDF (2/3 Pages) Sharma Electro Components,Inc – SH Series

CAPACITORS
TANTALUM DIPPED SH
ENDURANCE
Test Time/Hr
Leakage Current/µA
Capacitance/µF
Tan ∂
2000 ± 48
Less than 125% of initial value
Within ± 10% of initial value
Less than or equal to initial value
TAN ∂
Capacitance/µF
Tan ∂
0.1 to 1.5 2.2 to 6.8 10 to 68 100 to 220
0.04
0.06
0.08
0.1
IMPEDANCE (ohms MAX.)
V 6.3 10 16 25 35 50
µF
0.1
26.0 26.0
0.15
21.0 21.0
0.22
17.0 17.0
0.33
15.0 15.0
0.47
13.0 13.0
0.68
10.0 10.0
1.0
10.0 8.0 8.0
1.5
10.0 8.0 6.0 5.0
2.2
13.0 8.0 6.0 5.0 3.5
3.3
13.0 10.0 6.0 5.0 4.0 3.0
4.7
10.0 8.0 5.0 4.0 3.0 2.5
6.8
8.0 6.0 4.0 3.1 2.5 2.0
10
6.0 5.0 3.2 2.5 2.0 1.6
15
5.0 3.7 2.5 2.0 1.6 1.2
22
3.7 2.7 2.0 1.5 1.3 1.0
33
3.0 2.1 1.6 1.2 1.0
47
2.0 1.7 1.3 1.0 0.8
68
1.8 1.3 1.0 0.8
100
1.6 1.0 0.8
150
0.9 0.8 0.6
220
0.9 0.6 0.5
330
0.7 0.5
Impedance measured at 100KHz and 25˚C.
ELECTRICAL
Stability at
Temperature Extremes
Humidity 40˚C,
90-95% RH 21 days
Shelf Life
-55˚C Capacitance within ± 12% max
(better than -5% typ) +85˚C
Capacitance within ± 12% max (better
than +5% typ). Leakage current within
10% initial value.
Capacitance within 10% of initial value.
Leakage current within 125% of initial
value.Tan ∂ less than or equal to initial
value.
Capacitance within 10% of initial value.
2000Hr @ 85˚C; no
voltage applied
Surge Voltage 1000
cycles @ 85˚C
Rated Voltage/V
Surge Voltage/V
Temperature - Voltage
de-rating @ 125˚C
Leakage current within125% of initial
value. Tan ∂ less than or equal to initial
value.
Capacitance within 5% of initial value.
Leakage current less than or equal to
initial value. Tan ∂ less than or equal to
initial value.
6.3 10 16 25 35 50
8 13 20 32 44 63
6.3 10 16 25 35 50
4 6.3 10 16 23 33
SAFETY
Operating Properties
It is recommended that the following operating modes are not
imposed on the capacitors;
Over or reverse voltage
Over temperature
Power rating exceeded
High current surge due to low impedance (we recommend
that the circuit impedance should be 3Ω/V minimum).
Material Content
Tantalum capacitors contain no material normally considered as
hazardous. Materials include: Epoxy Resin, Graphite, Manganese
Dioxide, Tantalum, Tantalum Oxide. Noxious fumes may be emitted
if incinerated.