ST413PHA Datasheet, PDF (1/2 Pages) Coilcraft lnc. – Power Inductor for Critical Applications

1008 POWER INDUCTORS
Power Inductor for Critical Applications ST413PHA
■ Shielded power inductors
■ Excellent current handling for a part this size; low DCR
Core material Ceramic/Ferrite
Terminations  Silver-palladium-platinum-glass frit. Other termina-
tions available at additional cost.
Weight  122 – 132 mg
Ambient temperature  –40°C to +105°C with Irms current, +105°C
to +145°C with derated current
Storage temperature  Component: –55°C to +105°C.
Packaging: –55°C to +80°C
Resistance to soldering heat  Max three 40 second reflows at
+260°C, parts cooled to room temperature between cycles
Temperature Coefficient of Inductance (TCL)  +100 to +350 ppm/°C
Moisture Sensitivity Level (MSL)  1 (unlimited floor life at <30°C /
85% relative humidity)
Packaging  750/7²reel; 2500/13² reel  Plastic tape:  12 mm wide,
0.3 mm thick, 8 mm pocket spacing, 3.3 mm pocket depth

Inductance ^  DCR^{4  } SRF⁵
  _{Isat (A)}6 _{     Irms (A)}7
^  ±10%² Q max typ 10% 20% 30% 20°C 40°C
  _{Part number}1
(µH) ^  min³ (Ohms) (MHz) drop drop drop rise rise
ST413PHA102KLZ
ST413PHA152KLZ
ST413PHA182KLZ
ST413PHA222KLZ
ST413PHA272KLZ
1.0 35
1.5 35
1.8 35
2.2 36
2.7 38
0.05 387
0.06 276
0.09 253
0.10 228
0.14 207
3.5 3.9 4.2 1.4 2.0
2.7 3.2 3.5 1.4 2.0
2.3 2.7 3.0 0.98 1.4
2.4 2.8 3.1 1.2 1.7
1.6 2.0 2.3 1.0 1.4
ST413PHA332KLZ
ST413PHA392KLZ
ST413PHA472KLZ
ST413PHA562KLZ
ST413PHA682KLZ
3.3 26
3.9 38
4.7 38
5.6 38
6.8 38
0.84 199
0.26 185
0.35 160
0.36 150
0.58 120
1.5 1.6 1.6 0.51 0.67
1.5 1.8 2.0 0.82 1.1
1.3 1.6 1.7 0.70 0.95
1.5 1.7 1.8 0.66 0.87
1.3 1.5 1.6 0.45 0.76
ST413PHA103KLZ 10 38 0.92 105 0.84 1.0 1.1 0.40 0.59
ST413PHA153KLZ 15 38 1.15 35 0.81 0.87 0.90 0.36 0.51
ST413PHA223KLZ 22 40 1.40 26 0.67 0.75 0.79 0.33 0.44
ST413PHA333KLZ 33 45 1.61 20 0.53 0.61 0.68 0.30 0.42
ST413PHA393KLZ 39 45 1.85 16 0.49 0.56 0.60 0.28 0.39
ST413PHA473KLZ 47
ST413PHA683KLZ 68
ST413PHA823KLZ 82
ST413PHA104KLZ 100
ST413PHA124KLZ 120
45 2.5
45 3.8
45 4.3
45 5.8
50 6.3
19 0.47 0.52 0.54 0.23 0.31
12 0.38 0.42 0.45 0.21 0.26
9.0 0.33 0.38 0.42 0.18 0.26
7.0 0.35 0.38 0.39 0.16 0.20
7.0 0.30 0.33 0.35 0.14 0.20
ST413PHA154KLZ 150
ST413PHA224KLZ 220
ST413PHA334KLZ 330
ST413PHA474KLZ 470
ST413PHA564KLZ 560
50 7.5
55 10.0
55 11.5
55 16.3
55 18.1
5.8 0.27 0.30 0.33 0.13 0.18
5.0 0.21 0.24 0.27 0.13 0.17
3.8 0.19 0.21 0.23 0.11 0.15
3.1 0.14 0.17 0.19 0.10 0.13
2.8 0.13 0.15 0.17 0.093 0.12
ST413PHA684KLZ 680
ST413PHA824KLZ 820
ST413PHA105KLZ 1000
55 24.0
45 26.0
45 29.0
2.5 0.11 0.15 0.17 0.073 0.11
1.5 0.10 0.12 0.13 0.073 0.10
2.0 0.11 0.13 0.14 0.070 0.10
1. When ordering, specify termination and testing codes:
ST413PHA334KLZ
Termination: L = RoHS compliant silver-palladium-
platinum-glass frit.
Special order:
T = RoHS tin-silver-copper
(95.5/4/0.5) or S = non-RoHS tin-
lead (63/37).
Testing: Z = COTS
H= Screening per Coilcraft CP-
SA-10001
2. Inductance measured at 100 kHz, 0.1 Vrms, using
Coilcraft SMD-A fixture in Agilent/HP 4263B imped-
ance analyzer or equivalent.
3. Q measured at 1 MHz using an Agilent/HP 16193 test
fixture and an Agilent/HP 4291 or equivalent.
4. DCR measured on micro-ohmmeter and Coilcraft
CCF840 test fixture.
5. SRF measured using a Coilcraft SMD‑D test fixture
and an Agilent/HP 8753D network analyzer or equiva-
lent.
6. DC current at which the inductance drops the specic-
fied amount from its value without current.
7. Current that causes the specified temperature rise
from 25°C ambient.
8. Electrical specifications at 25°C.
Refer to Doc 362 “Soldering Surface Mount Compo-
nents” before soldering.
© Coilcraft, Inc. 2011
®
Specifications subject to change without notice.
Please check our website for latest information. Document ST219-1  Revised 03/08/11
1102 Silver Lake Road
Cary IL 60013
Phone [phone]
Fax [phone]
E-mail [e-mail]
Web www.coilcraft-cps.com