FCP0603C101J-K1 Datasheet, PDF (1/6 Pages) Cornell Dubilier Electronics – Surface Mount Film Capacitors

Type FCP Surface Mount Film Capacitors
Stable Stacked Metallized Film (PPS) Chips for Reflow Soldering
The Type FCP’s combination of high capacitance density
and excellent high frequency response makes it a great
choice for wireless and instrumentation applications.
Highlights
Type FCP stacked metallized polyphenelene sulfide (PPS) film capacitors offer high
capacitance per unit volume, stable capacitance and DF over a wide temperature
range, and excellent high frequency performance. Type FCP capacitors conform to
standard EIA 0603, 0805, 1206, 1210, 1913 & 2416 surface mount case sizes and
are packaged on tape and reel.
Specifications
♦ Stacked metallized polyphenylene sulfide (PPS) film.
♦ High operating temperature to +125 ºC
♦ High capacitance per unit volume
♦ Excellent high frequency performance
♦ Capacitance change from –55 ºC to 105 ºC ≤ ±1.5%
♦ Stable cap and DF over wide temperature range
Nominal Capacitance Range:
Capacitance Tolerance:
Rated Voltage:
Dissipation Factor (Tan d):
Operating Temperature Range:
Dielectric Strength:
Insulation Resistance:
Construction:
100 pF to 0.22 µF (1kHz at ≤5 Vrms)
±5% (J) Standard, ±2% (G) Optional
16 Vdc and 50 Vdc
0.6% Max. (1 kHz at ≤5 Vrms)
–55 ºC to +125 ºC (See Voltage derating chart for
0.12 - 0.22 µF above 105 ºC)
175% of rated Vdc for 5 seconds
3000 MΩ Min. at 20 ºC, after 60 seconds (16 Vdc
rated, test 10 Vdc; 50 Vdc rated, test 50 Vdc)
Stacked metallized polyphenylene sulfide (PPS)
film
Life Test:
Capacitors subjected to 1000 hours of maximum
rated temperature and 125% of the rated voltage
will not have any significant visual damage,
thecapacitance will be within ±2% of the initial
measured value, DF will be a maximum of 0.66%,
and IR will be a minimum of 1000 Megohms.
Resistance to Soldering Heat:
Capacitors subjected to a 260 °C reflow soldering
for 5 seconds will not have any significant visual
damage, dielectric strength will be as specified,
the capacitance will be within ±3% of the initial
measured value, DF will be a maximum of .66%,
and IR will be a minimum of 1000 Megohms.
Complies with the EU Directive
2002/95/EC requirement
restricting the use of Lead (Pb),
Mercury (Hg), Cadmium (Cd),
Hexavalent chromium (Cr(VI)),
PolyBrominated Biphenyls (PBB)
and PolyBrominated Diphenyl
Ethers (PBDE).
Moisture Resistance:
Capacitors subjected to 1000 hours at 40 °C and
90% to 95% RH and rated voltage will not have any
significant visual damage, will withstand 1.3 times
the rated voltage for one minute, the capacitance
will be within ±2% of the initial measured value,
DF will be a maximum of 0.9%, and IR will be a
minimum of 1000 Megohms.