AQ147A120JAJME Datasheet, PDF (2/4 Pages) AVX Corporation – Microwave MLC’s

Microwave MLC’s
AQ Series
ELECTRICAL SPECIFICATIONS
AQ11, AQ12, AQ13, AQ14
Temperature Coefficient (TCC)
Capacitance Range
Operating Temperature
Quality Factor (Q) M Dielectric A & B Case
A Dielectric B Case
A Dielectric A Case
Insulation Resistance (IR)
Working Voltage (WVDC)
Dielectric Withstanding Voltage (DWV)
Aging Effects
Piezoelectric Effects
Capacitance Drift
M&A
(M) +90 ± 20 PPM/ºC ( -55ºC to +125ºC)
(M) +90 ± 30 PPM/ºC ( +125ºC to +175ºC)
(A) 0 ± 30 PPM/ºC
(M) 0.1 pF to 1000 pF
(A) 0.1 pF to 5100 pF
0.1 pF to 330 pF: from -55ºC to +175ºC
360 pF to 5100 pF: from -55ºC to +125ºC
Greater than 10,000 at 1 MHz
Greater than 10,000 at 1 MHz
Greater than 2,000 at 1 MHz
Greater than 2,000 at 1 KHz
Greater than 10,000 at 1 MHz
Greater than 2,000 at 1 MHz
0.1 pF to 470 pF
10⁶ Megohms min. @ 25ºC at rated WVDC
10⁵ Megohms min. @ 125ºC at rated WVDC
510 pF to 5100 pF
10⁵ Megohms min. @ 25ºC at rated WVDC
10⁴ Megohms min. @ 125ºC at rated WVDC
See Capacitance Values table
250% of rated WVDC for 5 secs
(for 500V rated 150% of rated voltage)
None
None
± (0.02% or 0.02 pF), whichever is greater
C
±15% (-55ºC to 125ºC)
0.001μF to 0.1μF
-55°C to +125°C
2.5% @ 1kHz
0.1 - 200 pF
220 - 1000 pF
1100 - 5100 pF
0.1 - 100 pF
110 - 1000 pF
10⁴ Megohms min. @ 25ºC at rated WVDC
10³ Megohms min. @ 125ºC at rated WVDC
See Capacitance Values table
250% of rated WVDC for 5 secs
<3% per decade hour
None
Not Applicable
ENVIRONMENTAL CHARACTERISTICS
AVX SQLB will meet and exceed the requirements of EIA-198, MIL-PRF-55681 and MIL-PRF-123
Themal Shock
Mil-STD-202, Method 107, Condition A
Moisture Resistance
Mil-STD-202, Method 106
Low Voltage Humidity
Mil-STD-202, Method 103, condition A, with 1.5 VDC
applied while subjected to an environment of 85ºC with
85% relative humidity for 240 hours
Life Test
Mil-STD-202, Method 108, for 2000 hours at 125ºC
Shock
Mil-STD-202, Method 213, Condition J
Vibration
Mil-STD-202, Method 204, Condition B
Immersion
Mil-STD-202, Method 104, Condition B
Salt Spray
Mil-STD-202, Method 101, Condition B
Solderability
Mil-STD-202, Method 208
Terminal Strength
Mil-STD-202, Method 211
Temperature Cycling
Barometric Pressure
Mil-STD-202, Method 102, Condition C
Mil-STD-202, Method 105, Condition B
9
Resistance to Solder Heat
Mil-STD-202, Method 210, Condition C
157